具乙烯官能基之立方結構中孔洞材料 FDU-12 與 SBA-1 的合成與鑑定;Synthesis and Characterization of Cubic Mesoporous Silicas FDU-12 and SBA-1 with Vinyl Functionality

NCU Institutional Repository > 理學院 > 化學研究所 > 博碩士論文 > Item 987654321/6149

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/6149

題名:	具乙烯官能基之立方結構中孔洞材料 FDU-12 與 SBA-1 的合成與鑑定;Synthesis and Characterization of Cubic Mesoporous Silicas FDU-12 and SBA-1 with Vinyl Functionality
作者:	吳俊達;Jyun-Da Wu
貢獻者:	化學研究所
關鍵詞:	乙烯;官能基;中孔;複合;材料;mesoporous;silica;Fm3m;Ia3d;hybrid;FDU-12;SBA-1;functionalized;vinyl
日期:	2005-06-29
上傳時間:	2009-09-22 10:14:05 (UTC+8)
出版者:	國立中央大學圖書館
摘要:	摘要在室溫及酸性條件下，以四乙氧基矽酸鹽 (TEOS) 與三甲氧基乙烯基矽酸鹽 (TMVS) 作為共同矽源，分別使用三嵌段高分子 Pluronic F127 與溴化16基三乙氧基銨 (CTEABr) 作為主要模板試劑，以直接合成法製備結構排列整齊、具有立方、中孔洞並含有乙烯官能基的二氧化矽材料 FDU-12 (Fm3m) 與 SBA-1 (Pm3n)。乙烯官能基的含量可藉由固態 13C 與 29Si 核磁共振光譜加以證明。而相較於直接合成乙烯官能基化的SBA-15，乙烯官能基化的 FDU-12 與 SBA-1 其乙烯官能基含量分別可達到 30 % 與 25 % 而不會對中孔洞立方結構造成損壞或無法控制的相轉變。乙烯官能基化 FDU-12 其C=C雙鍵可輕易吸附 Methyl methacrylate (MMA) 而在孔洞中進行高分子聚合反應。乙烯官能基化 SBA-1 的中孔洞結構在 HCl/EtOH 溶劑萃取處理下較純 SBA-1 來得規則而穩定。 Abstract Direct synthesis of well-ordered cubic mesoporous silicas FDU-12 (Fm3m) and SBA-1 (Pm3n) with vinyl functionality were direct-synthesized via room temperature co-condensation of tetraethoxysilane (TEOS) and trimethoxyvinylsilane (TMVS) major templated with tri-block copolymer Pluronic F127 and cetyltriethylammonium bromide (CTEABr) under acidic conditions, respectively, has been achieved. Qualitative evidence of the presence of chemically attached vinyl moieties was provided by solid-state 13C and 29Si NMR. In contrast to the direct synthesis of vinyl-functionalized SBA-15, the concentration of TMVS that co-condensed with TEOS could be up to 30% and 20% without observing significant loss in the long-range mesostructural ordering and uncontrollable phase transformation of the vinyl-functionalized FDU-12 and SBA-1, respectively. The C=C double bonds of vinyl groups on v-FDU-12 are readily accessible to adsorbed methylmethacrylate (MMA) to induce polymerization within the mesopores. Vinyl-functionalized SBA-1 materials have a better ordered and stable structure towards the treatment with the solvent extraction (HCl/EtOH) than the pure silica SBA-1 without any functionality.
顯示於類別:	[化學研究所] 博碩士論文