高溫燒結含矽質再生材料在混凝土中的膨脹行為研究;Expansive Behavior of the Recycled Materials Contained Sintered Silica Used as the Aggregate in Concrete

NCUIR > Engineering College > Department of Civil Engineering > Research Project > Item 987654321/62197

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/62197

Title:	高溫燒結含矽質再生材料在混凝土中的膨脹行為研究;Expansive Behavior of the Recycled Materials Contained Sintered Silica Used as the Aggregate in Concrete
Authors:	李釗
Contributors:	國立中央大學土木工程學系
Keywords:	土木水利工程
Date:	2012-12-01
Issue Date:	2014-03-17 11:19:22 (UTC+8)
Publisher:	行政院國家科學委員會
Abstract:	研究期間：10108~10207;This two-year project plans to study the expansive behavior of recycled materials contained sintered silica, such as waste glass, waste tile, sintered light aggregate, and slag, used as the aggregate in concrete. The expansion of this kind recycled material may result from the alkali-aggregate reaction due to the amorphous silica contained in the material act as reactive aggregate, or from the slow hydration of hard burned calcium oxide or magnesium oxide. In the first year, this research plans to investigate the reactivity of the recycled materials according to ASTM C289, C227 and C1260, exam the pessimum effect of content and particle size of the identified reactive materials, and study the strategy for preventing expansion. In the second year, the slow hydration of CaO and MgO contained in the slag will try to be accelerated by breaking to the range of sand and cured in the moist environment. A mortar bar expansion test will be developed to identify the stability of slag on expansion. The expansive behavior of mortar bar samples will test in the conditions of 150℃ autoclave chamber, 100℃ steamed case and boiling water. The relationship among the slag particle size, temperature and curing time will be established in the process of slag stabilization.
Relation:	財團法人國家實驗研究院科技政策研究與資訊中心
Appears in Collections:	[Department of Civil Engineering] Research Project

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	303	View/Open

社群 sharing

Loading...