    题名: 聚(偏氟乙烯-三氟乙烯)薄膜的結構解析與感光壓電性質之研究;Structural-resolved Study of Photon-sensitive Piezoelectric Properties of P(VDF-TrFE) Films
    作者: 廖孜康;Liao,Tzu-Kang
    贡献者: 化學工程與材料工程學系
    关键词: 壓電材料;即時廣角繞射;同步輻射光源;P(VDF-TrFE);Pizoelectric;in-situ x-ray
    日期: 2014-07-21
    上传时间: 2014-10-15 14:36:22 (UTC+8)
    出版者: 國立中央大學
    摘要: 本研究使用即時同步X光繞射同時量測高分子壓電材料P(VDF-TrFE)與摻入的感光材料TiOPc 隨外加溫度,電場和感光作用下的微結構演變進一步區分出隨著溫度、電壓或照光時間控制的效能-結構關係。複合材料相變化時,各相繞射峰強度改變和晶格應變是本研究發現最具相關性的數據。隨各上述變因改變的過程中,微結構的變化,清楚的顯示了(一)相變化對應溫度;(二)晶格應變反應出電壓和感光的效應。本研究並進一步的量化電壓和照光所造成的晶面間距改變對巨觀整體效能的貢獻,以探討P(VDF-TrFE)/TiOPc的製程差異引入的微結構如何改善性能。最後從各種材料(有/無極化,有/無摻TiOPc) 對上述效應的不同反應,進一步去推論造成 P(VDF-TrFE)/TiOPc 巨觀壓電係數 (d33) 改變的原由。我們的結論是(一)極化 (poling)製程可以強化TiOPc與P(VDF-TrFE)彼此的作用力,極化過的薄膜於繞射結果中,受電場與感光控制產生的波動比未極化的薄膜低;(二)摻入TiOPc後,顯著的影響薄膜的壓電性能;(三)TiOPc以感光特質對P(VDF-TrFE)提升對電場的敏感度。;Semi-crystalline polymer, Poly(vinylidene fluoride-co-trifluoroethylene) coupled with TiOPc powder, which has excellent sensitivity to visible light, is expected to bridge photo sensor and piezoelectric actuators. This composite material does not only retains good piezoelectric efficiency and possesses high sensitivity to visible light. The beta-phase P(VDF-TrFE) exhibits a good piezoelectric property. Our sample is composed of P(VDF-TrFE) and with and without TiOPc, respectively. When the samples were heated continuously, applied electrical voltage, light illumination, we used in-situ XRD to measure the microstructure evolution. In this study, we investigated the phase transition induced by heating up to 90℃. We observed the changes of lattices distance subjected to temperature, electric field and light illumination. We also measured the bulk (piezoelectric properties) d33. We found a linear correlation between the macroscopic d33 and microscopic lattice strain. Our equation can well describe the d33 variation and lattice evolution subjected to various temperature and voltages.
    显示于类别:[化學工程與材料工程研究所] 博碩士論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML446检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明