English  |  正體中文  |  简体中文  |  Items with full text/Total items : 65275/65275 (100%)
Visitors : 20910458      Online Users : 216
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/65989


    Title: 環境效應對固態氧化物燃料電池接合件機械性質之影響;Environmental Effects on the Mechanical Properties of Joints in Solid Oxide Fuel Cell
    Authors: 劉育安;Liu,Yu-an
    Contributors: 機械工程學系
    Keywords: 燃料電池;機械性質;環境效應
    Date: 2014-08-21
    Issue Date: 2014-10-15 17:20:08 (UTC+8)
    Publisher: 國立中央大學
    Abstract: 本研究目的在探討還原環境對於玻璃陶瓷和金屬連接板接合件的接合強度及破壞模式的影響,所使用的玻璃陶瓷為核能研究所開發一款代號為GC-9的材質,金屬連接板則是使用代號為Crofer 22 H的商用肥粒鐵系不銹鋼。藉由製作兩款三明治試片,分別量測接合件在室溫與800 oC還原環境下的剪力及張力強度,同時評估還原環境時效處理對接合件強度的影響,並比較在還原環境與氧化環境下接合件所受之影響。
    結果顯示,經一千小時還原環境時效處理的剪力試片,在常溫下接合強度比未經時效處理之試片增加24%,而在高溫下則下降19%;張力試片的接合強度亦有相同之趨勢,與未時效相比較,時效處理後接合強度在常溫下增加與高溫下減少的幅度分別為47%與51%。時效處理後常溫接合強度增加的主因可能為:(1) 時效熱處理的過程中,改變GC-9玻璃陶瓷基材中缺陷的大小、形貌;(2) 時效熱處理時有應力鬆弛的現象;(3) 時效熱處理後,GC-9玻璃陶瓷結晶化程度提高。而在時效處理後,高溫下接合強度降低的主因為時效熱處理時,在GC-9玻璃陶瓷基材中的玻璃相與結晶相之間形成微孔洞所導致。
    由微結構及破斷面分析結果發現,接合件試片有四種破壞模式:(1) 破裂發生在玻璃陶瓷基材的內部;(2) 脫層現象發生於玻璃陶瓷基材與鉻酸鋇層的界面;(3) 脫層現象發生於金屬連接板與氧化鉻層的界面;(4) 破裂發生於玻璃陶瓷/鉻酸鋇/氧化鉻的混和層內。將微結構及破斷面分析結果與接合強度做比對,發現當破裂只發生於玻璃陶瓷基材的內部時通常伴隨的較高的接合強度,而破裂發生於界面或混和層時會有較低的接合強度。
    在還原環境與氧化環境下,未時效試片的接合強度與破壞模式並未有明顯差異,而在一千小時長時效處理後,還原環境與氧化環境皆會降低試片之接合強度,下降的幅度皆為19%。
    ;The objective of this study is to investigate the effect of reducing environment on the mechanical properties of a joint between a glass-ceramic sealant and an interconnect steel. A technique is developed for measuring the joint strength between glass-ceramic and metallic interconnect under tensile or shear loading in reducing environment at room temperature and 800 oC. The applied materials are a GC-9 glass-ceramic developed at the Institute of Nuclear Energy Research (INER) and a commercial Crofer 22 H ferritic stainless steel. Comparison of oxidizing and reducing environment effects on mechanical properties of a joint are also presented for variously, thermally aged conditions.
    Both tensile and shear joint strengths are increased at room temperature and decreased at 800 oC after a reducing aging treatment. A reducing aging treatment at 800 oC for 1000 h enhances the joint strength of shear loading at room temperature by 24% and degrades it at 800 oC by 19%. A reducing aging treatment at 800 oC for 1000 h increases the joint strength of tensile loading at room temperature by 47% and deterioriates it at 800 oC by 51%. Promotion of joint strength at room temperature may be related to changes in the flaw size and morphology, relaxation of residual stresses, and a greater extent of crystallization during aging treatment. Degradation of joint strength at 800 oC is probably due to formation of micro-voids between crystalline and glassy phases after aging treatment.
    Through fractography anaysis, fracture mode of the joint is correlated with the measured fracture strength. Four types of fracture modes are identified for the joint specimens. Firstly, fracture occurs within the glass-ceramic layer. Secondly, delamination takes place at the interface between the GC-9 glass-ceramic sealant and a chromate layer. Thirdly, delamination occurs at the interface between the metal substrate and a Cr2O3 layer. Fourthly, fracture involves cracking in the interfacial mixed layer of glass-ceramic/chromate/chromia. A greater joint strength is accompanied by cracking within the glass-ceramic layer, while a lower joint strength corresponds to fracture involving interfacial delamination or cracking in the interfacial mixed layer of glass-ceramic/chromate/chromia.
    The joint strength and fracture mode are comparable between the given reducing and oxidizing environments for non-aged specimens. Thermal aging treatments in both given environments have detrimental effects on the joint strength at 800 °C. Compared to the shear strength of the non-aged specimens, 19% of reduction in strength is both observed for the specimens exposed to the given reducing and oxidizing environments.
    Appears in Collections:[機械工程研究所] 博碩士論文

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML244View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明