English  |  正體中文  |  简体中文  |  Items with full text/Total items : 65317/65317 (100%)
Visitors : 21354791      Online Users : 460
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/6707


    Title: 低溫製作大晶粒複晶矽薄膜之研究;Fabrication of Poly-Silicon Thin Films at Low Temperature by PECVD
    Authors: 彭智宏;Zhi-Hong Peng
    Contributors: 光電科學研究所
    Keywords: 化學氣相沉積法;多晶矽薄膜;低溫;low temperature;poly-silicon thin films;PECVD
    Date: 2002-07-10
    Issue Date: 2009-09-22 10:26:22 (UTC+8)
    Publisher: 國立中央大學圖書館
    Abstract: 本實驗採用自行設計組裝的高週波偏壓輔強射頻感應耦合電漿輔助化學氣相沉積系統,用矽烷/氫氣/氬氣等氣體為原料,在玻璃基板及矽基板上於低溫(<50 ℃)合成矽薄膜,研究不同參數對薄膜的影響及沉積矽薄膜的最佳參數。所得之矽薄膜以探針測厚儀量測薄膜厚度、傅立葉轉換紅外光光譜儀分析薄膜的鍵結結構、掃描式電子顯微鏡來觀察薄膜表面形態及結晶尺寸、拉曼光譜儀測量薄膜的鍵結狀態、 X光繞射分析儀分析薄膜的結晶結構及其方向性。 經實驗發現最佳參數為SiH4分壓為20 mTorr,H2分壓為40 mTorr,Ar分壓為40 mTorr,高週波能量(W1)為90 watts,輔助偏壓能量(W2)為10 watts,可成長出晶粒尺寸高達0.6 μm的大晶粒矽薄膜。
    Appears in Collections:[光電科學研究所] 博碩士論文

    Files in This Item:

    File SizeFormat
    0KbUnknown536View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明