    题名: 偏光片新材料開發階段多目標優化之穩健設計;Multi-Criteria Robust Design for New Material Development stage of Polarizing Film
    作者: 毛子軒;MAO,TZYY-SHIUAN
    贡献者: 工業管理研究所在職專班
    关键词: 穩健設計;田口方法;多目標;偏光片
    日期: 2015-06-22
    上传时间: 2015-07-30 18:08:05 (UTC+8)
    出版者: 國立中央大學
    摘要: 偏光片發展面臨高品質要求與價格競爭,於開發設計除了考量提高光學優異性、薄型化,不外乎以降低生產成本或開發新材料為幾個主要發展目標。本研究在新產品先進技術設計開發之架構下,運用協同設計系統化之概念發展替代新材料。結合研發、品質、工程、製造各部門參與進行產品開發,以穩健設計概念與統計分析手法進行參數設計,達到偏光片新材料設計開發階段,能穩定其研磨端面缺陷的品質目標且縮小變異後量產。
    本研究針對偏光片在新材料應用後進行端面研磨的缺陷作探討,端面研磨品質特性有兩種:表面處理碎裂與三層剝離,此二缺陷皆為望小目標,故進行多目標最佳化配置。首先以魚骨圖分析品質缺陷特性要因,找出潛在影響因子做第一次實驗分析,實驗結果模型解釋力R-Square約80%,依實驗結果選定影響因子之最佳參數後做第二次實驗,以期有更好的結果。兩次實驗皆分別運用田口方法做S/N ratio分析、平均值分析、柏拉圖最適前緣與參數應用原理原則等不同之方法,搭配成本和效益,進行多目標最佳化結果之分析比較,最後以模型估計之信賴區間做驗證,得到既精又準的實驗結果。以顯微鏡進行偏光片端面缺陷觀察,最佳化操作水準之品質特性AG crack由200um降低至46um。3L peeling由250um降低至66um。同時變異也縮小到17um與5um,有顯著的優化改善。
    此新材料產品在偏光片材料應用上具有象徵性指標之技術意義,並代表材料供應鏈和成本的變化,達成階段性代表產品的重要目標任務。期望能帶給後續各產品於開發階段,即進行穩健設計分析之實務應用作為參考,避免於產品量產之後因變異問題進行大幅修改導致損失,也同時避免端面缺陷造成客訴或衍生產品應用問題。
    ;The polarizer industry has officially entered an era of high quality demand and intense price competition. Other than improving performance and enhancing the slimness of the product, the R&D of companies in this industry focuses on cost reduction or new material discovery. Under the structure of Advanced Product Quality Planning of new product development, this research applies the concurrent engineering systematic concept to discover new product. With the cooperation of R&D, Quailty mangement, Engineering, and Production division, and the concept of robust decision and statistic analysis method, the new material development is capable of stabilizing the defects in grind process, minimizing the product defects variation, and allowing massive production.
    This study focuses on reducing defects of grind process after applying the new material. The two major defects are the surface crack and the third-layer peeling. In order to minimize the defects we apply the multi-criteria robust design. Through the cause-and-effect diagram, this research is able to identify the major characteristics of the defects and to locate the potential factors for the first-stage experiment, and the R-square of the results at this stage is about 80%. With the intention to have continuous improvement, the second-stage experiment is performed based on the optimized parameters from the first-stage results. All experiments applied the Taguchi Methods of Robust Design on S/N ratio analysis, mean analysis, Pareto frontier, and parameter application theorem. Furthermore, along with the cost and revenue relationship, these experiments also applied multi-criteria optimization comparision. Finally, confirmation experiments were performed to varify the proposed model. The optimal solution surface crack is reduced from 200um to 46um.Third-layer peeling is shorten from 250um to 66um. And the product defects variation is reduced from 17um to 5um.
    With the achievement of producing representative product at current stage and minimized material costs, this research on new-materialized polarizer product can be served as a benchmark on polarize material application technique. Moreover, this research can also be served as a reference for future study on robust design, which prevents further cost due to corrective activity on mass production stage, and avoids defects from grind process which might cause customers’ complain or application problems related to product.
    显示于类别:[工業管理研究所碩士在職專班 ] 博碩士論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML620检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明