English  |  正體中文  |  简体中文  |  Items with full text/Total items : 72271/72271 (100%)
Visitors : 23074286      Online Users : 559
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version

    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/69023

    Title: 6061鋁合金於累進式背擠製成型研究
    Authors: 鄭名翔;Cheng,Ming-hsiang
    Contributors: 機械工程學系
    Keywords: 6061;擠製
    Date: 2015-07-30
    Issue Date: 2015-09-23 14:55:16 (UTC+8)
    Publisher: 國立中央大學
    Abstract: 由劇烈塑性變形(Severe plastic deformation, SPD)方法達到超細晶粒(Ultrafine-grained, UFG)材料已被廣泛研究,本文採取由Fatemi-Varzaneh[20]等人提出的累進式背擠製(Acumulative back extrusion, ABE)於室溫對6061鋁合金加工。透過實驗與模擬,搭配不同的沖頭比(Deformation ratio,DR)與內沖頭行程(Die stroke,DS),並配合硬度、微觀結構與有限元素模擬分析,探討ABE擠製過程的機制,與不同實驗參數造成的效應。經由有限元素模擬分析與實驗結果比較獲得良好的一致性,DR與DS會影響材料加工硬化與硬度均勻程度的變化,而本研究中能夠產生奈米等級的晶粒,但大部分晶界仍保持在低角度,顯示在仍無法達到超細晶粒的要求。;To reach the ultrafine-grained(UFG) material from severe plastic deformation(SPD) method has been widely investigated.The present work used the AA60
    61 in the room temperture processing of accumulative back extrusion(ABE) that
    was one of the SPD techniqus was originally proposed by Fatemi-Varzaneh[20].
    To investigate the mechanics of the processing of the ABE using the experi-
    ment and the finite element method(FEM) with different deformatio ratio(DR),
    Die stroke(DS) and pass number.Then,the microhardness and the microstructure
    were utilized to study with the effective strain(ES) and shear strain(ES). Compa
    ring the FEM and experimental results showed good agreement in the ES conto-
    ur and microhardness. The DR and DS both has the great effect in the mechanic-
    al properties of the workpiece.Althrough the part the grain size has high ES thro-
    ugh one to three pass all can reach the nanoscale in the microstructure result,the
    most of grain boundaries still remained low anglar grain boundry.It means the high stacking fault energy of AA6061 through ABEed processing at room temp-
    erture still can’t satisfied with the UFG.
    Appears in Collections:[機械工程研究所] 博碩士論文

    Files in This Item:

    File Description SizeFormat

    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明