以CaTiO3應用於鈣鈦礦太陽能電池電子傳輸層之研究;The Study of Perovskite Solar Cells by Using Calcium Titanate as Electrical Transfer Layer

NCU Institutional Repository > 工學院 > 機械工程研究所 > 博碩士論文 > Item 987654321/72395

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/72395

題名:	以CaTiO3應用於鈣鈦礦太陽能電池電子傳輸層之研究;The Study of Perovskite Solar Cells by Using Calcium Titanate as Electrical Transfer Layer
作者:	林育葳;Lin,Yu-Wei
貢獻者:	機械工程學系
關鍵詞:	鈣鈦礦;太陽能電池;碳酸鈣;Perovskite;Solar cells;Calcium carbonate
日期:	2016-07-18
上傳時間:	2016-10-13 14:52:03 (UTC+8)
出版者:	國立中央大學
摘要:	本篇論文係利用 CaTiO3材料作為鈣鈦礦太陽能電池之電子傳輸層之研究，本實驗室技術已穩定製作出結構為 FTO/二氧化鈦(TiO2) 緻密層/二氧化鈦(TiO2)多孔隙層/CH3NH3PbI3主動層/Spiro-OMeTAD 電洞傳輸層/銀電極 Ag 作為標準片，此標準電池有著 Jsc=18.3mA/cm2， Voc=0.97V，FF=0.68，PCE=12.1%之光電轉換特性。鈣(Calcium)為地球中第五豐富的元素，日常生活中碰到許多材料如蛋殼、牡蠣皆為鈣化合物。實驗中以鈣鈦礦太陽能電池電子傳輸層 -二氧化鈦多孔隙層當中添加鈣元素來改善主動層 CH3NH3PbI3的成膜結晶性質，藉以提升開路電壓(Voc)。實驗中以碳酸鈣(CaCO3)及四氯化鈦(TiCl4)兩種材料作為反應成功合成出 CaTiO3/TiO2奈米顆粒。實際將 CaTiO3/TiO2奈米顆粒應用在鈣鈦礦太陽能電池之多孔隙層製作出鈣鈦礦太陽能電池有著 Jsc=13.7mA/cm2，Voc=0.99V， FF=0.62，PCE=8.4%之光電轉換特性。爾後為了改善使用 CaTiO3/TiO2奈米顆粒作為多孔隙層較低的短路電流，我們使用了兩次塗佈法增加了CaTiO3/TiO2奈米顆粒的覆蓋率，使得主動層 CH3NH3PbI3不輕易接觸到 FTO 玻璃形成短路，而增加覆蓋率使得多孔隙層與主動層 CH3NH3PbI3接觸表面積增加，電子有更佳的遷移率使得電流由原先的13.7 mA/cm2提升至16.2 mA/cm2，光電轉換效率更是由8.4%提升至 10.2%。;This study applies CaTiO3 as a mesoporous layer for Perovskite Solar Cells. We fabricated standard Perovskite Solar Cells as structure FTO/TiO2 compact layer/TiO2 mesoporous layer/ CH3NH3PbI3 active layer/Spiro-OMeTAD hole transfer layer/silver in both anode and cathode. This cell has Jsc=18.3mA/cm2, Voc=0.97V, FF=0.68 and PCE=12.1%。 Calcium is the 5th most abundant element in the world. We used calcium carbonate react with titanium dioxide and synthesized nano- CaTiO3/TiO2 powder as electrical transfer layer to enhance the crystallization of active layer (CH3NH3PbI3) and the turn-on voltage. Moreover, using nano-CaTiO3/TiO2 powder as a mesoporous layer of Perovskite Solar Cells and it performs Jsc=13.7mA/cm2, Voc=0.99V, FF=0.62 and PCE=8.4%. To extract the short-circuit current, we improve the coverage of mesoporous layer on FTO surface via two step spin-coating method. The mesoporous layer could avoid the active layer directly contacting FTO glass, which would result in short-circuit condition. In addition, the mobility of electrons would be enhanced due to the significant coverage of mesoporous layer. Which also increase the contact area between active layer and mesoporous layer. Consequently, increased contact area enhances the short-circuit current(Jsc) from 13.7 mA/cm2 to 16.2 mA/cm2 and also improves power conversion efficiency from 8.4% to 10.2%.