    題名: 三苯胺及 2,3-雙苯基喹啉的p型有機染料敏化太陽能電池之研究;Organic Dyes Containing Triphenylamine and 2,3-Diphenylquinoxaline for p-type Dye-Sensitized Solar Cells
    作者: 郭明中;Kuo, Ming-Chung
    貢獻者: 化學學系
    關鍵詞: p型有機染料敏化太陽能電池;三苯胺;2,3-雙苯基喹啉;p-type Dye-Sensitized Solar Cells;Triphenylamine;2,3-Diphenylquinoxaline
    日期: 2016-10-04
    上傳時間: 2017-01-23 16:06:18 (UTC+8)
    出版者: 國立中央大學
    摘要: 本論文設計並合成6個D–A–π–A 型式的EH系列p型有機染料,以一個或兩個羧酸根為錨固基團,三苯胺(triphenylamine)為推電子端,2,3-雙苯基喹啉(2,3-diphenylquinoxaline)為輔助拉電子片段,2-亞甲基丙二腈(2-methylenemalononitrile)為拉電子基團,中間分別以噻吩(thiophene)、3,4-ethylenedioxythiophene(EDOT)以及2,2′-聯噻吩(2,2′-bithiophene)為π共軛片段。可區分為含一個錨固基和兩個發色團的單錨染料(EH122、EH166、EH174),及兩個錨固基和一個發色基團的雙錨染料(EH126、EH162、EH170)。為探討不同的π共軛片段以及單錨雙錨結構對染料光電表現的影響,分別進行紫外光-可見光吸收光譜、螢光激發放射光譜、循環伏特安培法、EIS(electronchemical impedance spectroscopy)等實驗。
      同時將上述染料製作成p型染料敏化太陽能電池元件,利用 AM 1.5 irradiation(100 mW/cm2)太陽光模擬進行效能測試。
      結果顯示EH174有最佳的光電轉換效率η = 0.207%(Jsc = 4.84 mA/cm2, Voc = 137 mV, ff = 0.312),而含有EDOT片段的雙錨染料EH162為η = 0.062%,效果不大理想,推測可能原因是:莫耳消光係數相較單錨結構低,且在激發態的電荷分離較不明顯,導致整體效率下降。
      透過本論文對π共軛片段以及單錨雙錨染料結構和電池效能之間相關性的研究,希望未來能設計出更高效能的光捕獲材料。
    ;Six new p-type D–A–π–A dyes have been synthesized and studied. These dyes consist of one or two carboxylic acid as the anchoring group, triarylamine as the electron donor, 2,3-diphenylquinoxaline as the auxiliary acceptor moiety, 2-methylenemalononitrile as electron acceptor, connected with thiophene, 3,4-ethylenedioxythiophene(EDOT)and 2,2′-bithiophene as the π-spacor. It can be divided into one anchoring dye(EH122、EH166、EH174)and two anchoring dye(EH126、EH162、EH170). The influence of different π-spacor dye on photovoltaic performance were studied by UV/Vis, fluorescence spectroscopy, cyclic voltammetry and EIS(electronchemical impedance spectroscopy).
    The cell performances of cells assembled from these light-harvesting dyes have been evaluated using the AM 1.5 simulated solar light.
    The results showed that EH174 has the best power conversion efficiency of 0.207 %(Jsc = 4.84 mA/cm2, Voc = 137 mV, ff = 0.312)under AM 1.5 irradiation(100 mW/ cm2)whereas the two anchoring dye EH162(= 0.062%)with EDOT moiety was not as effective as expected perhaps due to low molar extinction coefficient compare to one anchoring dye, and charge separation is not obvious at excitation state which leads a low overall efficiency.
    A general correlation between the structural factors and the cell performances are currently under investigation aiming to provide a guideline for future design of high performance light-harvesting dyes.
    顯示於類別:[化學研究所] 博碩士論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML305檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright © National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋  - 隱私權政策聲明