中大機構典藏-NCU Institutional Repository-提供博碩士論文、考古題、期刊論文、研究計畫等下載:Item 987654321/72600
English  |  正體中文  |  简体中文  |  Items with full text/Total items : 66984/66984 (100%)
Visitors : 22917153      Online Users : 2241
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/72600


    Title: 利用火花電漿燒結製備鋁摻雜矽塊材之熱電性質研究;The study of thermoelectric properties for the aluminum doped silicon by Spark Plasma Sintering
    Authors: 曹森霖;Tsao, Sen-Lin
    Contributors: 材料科學與工程研究所
    Keywords: ;;火花電漿燒結;熱電性質;Silicon;Aluminum;Spark Plasma Sintering;thermoelectric properties
    Date: 2016-12-07
    Issue Date: 2017-01-23 16:35:19 (UTC+8)
    Publisher: 國立中央大學
    Abstract: 矽塊材在室溫下是高熱導率的材料,約150W/m*K,也因此純矽塊材為不良的熱電材料。為了提升熱電性質,球磨並添加摻雜元素是常見的方法,利用界面散射使熱導率下降,以摻雜提升電導率。
    本研究將矽顆粒和不同比例的鋁顆粒一起球磨,研磨24小時後利用火花電漿燒結成塊材,燒結時最高溫度約1000°C,低於矽燒結時常使用的溫度,藉鋁熔化後幫助顆粒之間的連接和提升矽的結晶性而可以讓燒結溫度降低到1000°C。燒結後的塊材進行熱電性質量測,溫度範圍為室溫至450°C,得知當鋁添加量是5at%以上時,導電率明顯提升,顯示添加5at%以上的鋁有顯著的摻雜效果,並得知添加5at%鋁有最好的熱電性質。
    ;The thermal conductivity of bulk silicon is 150 W/m*K at room temperature. It is considered as poor thermoelectric materials. Ball milling with doping is a common method for enhancing thermoelectric efficient.
    In our study, silicon and aluminum particles were milled in a ball mill bar with different ratio for 24 hours. After milling, the milled particles were fabricated into bulk samples via spark plasma sintering. The sintering temperature was 1000°C, which was lower than that often used in the sintering of silicon. The reason for the lower sintering temperature is that the molten aluminum can help the connection of silicon particles and enhance the crystallinity. After sintering, we measured the thermoelectric properties of bulk sintered sample from room temperature to 450°C. We found that the electrical conductivity was significantly improved when the aluminum exceeds 5at%. The result shows that addition of more than 5at% aluminum has significant doping effect and we found that the sintered bulk sample has the improved thermoelectric properties with the addition of aluminum of 5at%.
    Appears in Collections:[Institute of Materials Science and Engineering] Electronic Thesis & Dissertation

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML427View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明