應用高壓蒸氣技術製備抗菌輕質材料及其 特性評估研究;Characterization of anti-fungal lightweight material manufactured by autoclaving technique

NCU Institutional Repository > 工學院 > 環境工程研究所 > 博碩士論文 > Item 987654321/75166

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/75166

題名:	應用高壓蒸氣技術製備抗菌輕質材料及其特性評估研究;Characterization of anti-fungal lightweight material manufactured by autoclaving technique
作者:	戴肇寬;DAI, ZHAO-KUAN
貢獻者:	環境工程研究所
關鍵詞:	高壓蒸氣技術;漿紙污泥;氣化飛灰;淨水污泥;抗菌輕質化材料;Autoclaving;paper mill sludge;gasification ash;water purification sludge;antifungal lightweight materials
日期:	2017-08-22
上傳時間:	2017-10-27 16:24:07 (UTC+8)
出版者:	國立中央大學
摘要:	本研究應用高壓蒸氣技術，控制鈣矽比(0.6~1.49)、蒸氣壓力(0.4~0.8MPa)及反應時間(4~12hr)，並以市售奈米級二氧化鈦作為抗菌之調質劑(添加配比介於0~5%)，探討含鈣矽化合物之泥渣類廢棄物轉換為抗菌輕質化材料之可行性，研究對象分別為漿紙污泥氣化後之飛灰、漿紙污泥煅燒後之飛灰及淨水污泥。研究結果顯示，控制鈣矽比為0.9、蒸氣壓力0.8 MPa 及反應時間8小時之條件下，以氣化灰製備之材料具有較低之視密度(1.61 g/cm3)及較高之抗壓強度(32.4 kgf/cm2)，而以煅燒灰製備之材料，其視密度約為1.63 g/cm3，而抗壓強度稍低於氣化灰製備之材料，約為31.9 kgf/cm2。在添加二氧化鈦之調質試驗結果顯示，調整不同鈣矽比(0.6~1.49)及二氧化鈦添加比例(0~5%)條件下，以氣化灰製備之材料，具有低視密度(1.61~1.64 g/cm3)、高視孔隙率(53.0~57.3%)及高抗壓強度(34.7~85.5 kgf/cm2)等材料特性，符合相關高壓蒸氣養護輕質氣泡混凝土之產品規範。以氣化灰製備材料之環境安全性分析結果可知，材料之鉛、硒、鋅、鉻、砷、銅、鎘、鋇、鎳等重金屬TCLP濃度均符合法規標準。至於抗菌試驗之分析結果，經過14天之試驗後，輕質化材料表面之Penicillium funiculosum覆蓋率，由添加0% TiO2之66.36%降至添加5% TiO2之20.47%。另根據ASTM G21-09之材料抗黴目視等級評估規範，於14天照光試驗條件之抗菌等級，為第二級，此係本研究製備之輕質化材料添加二氧化鈦後，可透過光催化作用抑制Penicillium funiculosum生長，不僅降低Penicillium funiculosum之生長速率，更可減少該菌之生長面積，達到抑菌之效果。整體而言，本研究應用高壓蒸氣技術製備之抗菌輕質化材料極具未來應用與發展之潛力。 ;This study investigates the characterization of antifungal lightweight material produced from water purification sludge, ash derived from paper mill sludge gasification and combustion by autoclaving technique with controlled Ca/Si ratio 0.6~1.49, steam pressure 0.4~0.8 MPa and reaction time 4~12 hr. Commercialized nano-titanium dioxide (0~5%) was used as an antifungal modifier. In the case of Ca/Si ratio 0.9, steam pressure 0.8 MPa and reaction time 8 hr, the experimental results indicated that the lightweight material produced from gasification ash have a lower bulk density (1.61 g/cm3) and higher compressive strength (32.4 kgf/cm2). However, the lightweight material produced from combustion ash have a relatively high bulk density (1.63 g/cm3) and low compressive strength (31.9 kgf/cm2). In order to enhance the quality and performance of lightweight materials, in the case of 0~5% titanium dioxide addition and Ca/Si ratio controlled between 0.6 and 1.49, the characteristics results indicated that the lightweight materials produced from gasification ash have a lower bulk density (1.61~1.64 g/cm3), higher apparent porosity (53.0~57.3%) and higher compressive strength (34.7~85.5kgf/cm2). It was in compliance with relevant criteria of autoclaving lightweight concrete. According to the analysis results of environmental safety of lightweight material produced from gasification ash, it was shown that the tested toxic metals concentrations by toxicity characteristics leaching procedure (TCLP) were lower than the regulation thresholds in Taiwan. As the analysis results of the 14 days antifungal test, the lightweight materials surface coverage rate of Penicillium was decreased from 66.36% to 20.47% with titanium dioxide addition ratio increasing from 0% to 5%. Based on ASTM G21-09 standard method, in the case of light test after 14 days, the visible rating of the lightweight material was second grade. That is, adding titanium dioxide can inhibit Penicillium growth by photocatalytic. It can decrease the Penicillium growth rate and reduce surface coverage of lightweight material. In summary, the antifungal lightweight materials produced from gasification ash have been proven successfully by autoclaving technique. It has a good potential for building materials application and development in the future.