English  |  正體中文  |  简体中文  |  Items with full text/Total items : 67621/67621 (100%)
Visitors : 23050377      Online Users : 580
RC Version 7.0 © Powered By DSPACE, MIT. Enhanced by NTU Library IR team.
Scope Tips:
  • please add "double quotation mark" for query phrases to get precise results
  • please goto advance search for comprehansive author search
  • Adv. Search
    HomeLoginUploadHelpAboutAdminister Goto mobile version


    Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/76904


    Title: 提升P型Al0.5Ga0.5N歐姆接觸電極的導電性及反射率;Enhancing Conductance and Reflectivity of the Ohmic Contact to P-type Al0.5Ga0.5N
    Authors: 劉文獻;Liu, Wen-Hsien
    Contributors: 光電科學與工程學系
    Keywords: P 型氮化物
    Date: 2018-07-23
    Issue Date: 2018-08-31 11:52:58 (UTC+8)
    Publisher: 國立中央大學
    Abstract: P型氮化物半導體大多以鎳金(Ni/Au)作為歐姆接觸電極。對覆晶型(Flip-Chip)深紫外(deep utralviolet, DUV, 波長 ≤ 290 nm) LED來說,金在DUV波段的反射率不到30%,嚴重犧牲元件的光萃取效率。為了解決此問題,我們在DUV LED的P型電極上需克服兩大難題:(1) 提升金屬電極在DUV波段的反射率;(2)降低P型氮化鋁鎵(Al0.5Ga0.5N)表面的接觸電阻。
    在本研究中,我們以Ni/Al/Ti/Au取代Ni/Au。我們利用高真空電子束暨熱阻式蒸鍍系統 (E-gun/Thermal),在P型Al0.5Ga0.5N磊晶層上蒸鍍Ni/Al/Ti/Au,再分析退火溫度對Ni/Al/Ti/Au接觸電阻的影響。我們發現,550℃的退火溫度可將接觸電阻及片電阻分別從2.81x101 ohm-cm2及9.41x108 ohm/sq,降低至3.05x10-2 ohm-cm2及8.79x105 ohm/sq。在反射率方面,Ni/Al/Ti/Au在280 nm的反射率可達57%,遠高於Ni/Au的24%。雖然Ni/Al/Ti/Au的導電度有待改進,但由於Al的高UV反射率,可以補償其在電性上的損失。未來,我們將持續優化Ni/Al/Ti/Au的製程條件,希望能有效提升DUV LED的發光效率。
    ;Deep ultraviolet (DUV) LEDs traditionally employ Ni/Au as the ohmic contact to p-type AlGaN. However, for flip-chip devices, the reflectivity of gold at DUV wavelengths is below 30%, severely sacrificing the light extraction efficiency of DUV LEDs. To address the issues, there are two challenges to overcome with the p-type ohmic contact: (1) Increasing reflectivity in the DUV regime; (2) Decreasing the contact resistance on p-type Al0.5Ga0.5N.
    In this study, Ni/Au is replaced with Ni/Al/Ti/Au as the ohmic contact to p-type Al0.5Ga0.5N. The Al-based alloy was deposited by a high-vacuum electron-beam/thermal evaporation. The ohmic contact structure is then annealed at varied temperatures, with the attempt to reduce contact/sheet resistance. It is found that the annealing at 550 °C effectively reduces the specific contact resistance and the sheet resistance from 2.81x101 ohm-cm2 and 9.418x108 ohm/sq to 3.057x10-2 ohm-cm2 and 8.791x105 ohm/sq, respectively. For optical characterization, the reflectance of Ni/Al/Ti/Au at 280 nm reaches 57 %, significantly higher than that (24%) attained with Ni/Au. Although the conductivity of Ni/Al/Ti/Au on p-type Al0.5Ga0.5N remains to be improved, the high UV reflectivity is expected to compensate the loss in electrical performance. In the future, the fabrication of Ni/Al/Ti/Au will be optimized to enhance the external quantum efficiency of DUV LEDs.
    Appears in Collections:[光電科學研究所] 博碩士論文

    Files in This Item:

    File Description SizeFormat
    index.html0KbHTML52View/Open


    All items in NCUIR are protected by copyright, with all rights reserved.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback  - 隱私權政策聲明