Atmospheric-pressure plasma deposition of SiOx films for super-hydrophobic application

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26365

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26365

題名:	Atmospheric-pressure plasma deposition of SiOx films for super-hydrophobic application
作者:	Yang,SH;Liu,CH;Su,CH;Chen,H
貢獻者:	化學工程與材料工程學系
關鍵詞:	SILICON DIOXIDE FILMS;GLOW-DISCHARGE;SURFACES;NONEQUILIBRIUM;WETTABILITY;JET
日期:	2009
上傳時間:	2010-06-29 17:26:26 (UTC+8)
出版者:	中央大學
摘要:	In this study, we investigate the chemical proper-ties and surface morphology of super-hydrophobic (SH) films deposited by self-assembled RF atmospheric-pressure plasma (APP) deposition system. The O-2/HMDSN (hexamethyldisilazane) and At serve as the deposition precursor and ionization gas, respectively. The effects of process parameters, including the oxygen flow rate and the nozzle-to-sample distance on the characteristics of SiOx films measured by FTIR, XPS, SEM and AFM are also discussed. It was found that the higher deposition rate was obtained at higher oxygen flow rate conditions. Consequently, the smooth surface was transformed into a rough surface with many particles when the nozzle-to-sample distance was decreased from 20 mm to 10 mm. The SH films (contact angle over 150 degrees and sliding angle below 5 degrees) were obtained when the nozzle-to-sample distance was 10 mm. A simplified deposition mechanism is proposed to explain the effect of process parameters on the films that are formed. Crown Copyright (C) 2009 Published by Elsevier B.V. All rights reserved.
關聯:	THIN SOLID FILMS