Thermal and electrochemical behavior of yttria-stabilized zirconia coated LiCoO2 during overcharge tests

NCUIR > Engineering College > National Central University Department of Chemical & Materials Engineering > journal & Dissertation > Item 987654321/26451

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/26451

Title:	Thermal and electrochemical behavior of yttria-stabilized zirconia coated LiCoO2 during overcharge tests
Authors:	Fey,GTK;Hsiao,CL;Muralidharan,P
Contributors:	化學工程與材料工程學系
Keywords:	RECHARGEABLE LITHIUM BATTERIES;LI-ION CELL;CATHODE MATERIALS;ENHANCED CYCLABILITY;4.5 V;ELECTROLYTE;PERFORMANCE;IMPROVEMENT
Date:	2009
Issue Date:	2010-06-29 17:28:22 (UTC+8)
Publisher:	中央大學
Abstract:	Sol-gel synthesized yttria-stabilized zirconia (YSZ) ceramic powders were coated on LiCoO2 cathode particles by a simple mechano-thermal process, calcined at 923 K for 10 h. The XRD patterns of YSZ-coated LiCoO2 revealed a single-phase hexagonal alpha-NaFeO2-type structure with Rim symmetry of the core material without any modification. The surface of LiCoO2 particles was coated with a uniform layer of YSZ that had an average thickness of similar to 20 run, as observed from TEM images. The different binding energies of O 1 s XPS data exhibited the presence of oxygen ions corresponding to the surface coated YSZ and LiCoO2. The galvanostatic cycling studies for the coated materials suggest that 2.0 wt.% YSZ-coated LiCoO2 delivered a stable capacity of 160 mAh g(-1) between 2.75 V and 4.4 V vs. Li and a good cycle stability of about 142 cycles. The impedance growth was slower for LiCoO2 surface coated with YSZ, when cells were charged at 4.4 V and 4.5 V. DSC results illustrated that the oxygen evolution exothermic peak at about 458 K was significantly smaller for YSZ-coated cathode materials. (C) 2008 Elsevier B.V. All rights reserved
Relation:	JOURNAL OF POWER SOURCES
Appears in Collections:	[National Central University Department of Chemical & Materials Engineering] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	432	View/Open

社群 sharing

Loading...