题名:	Growth and characterization of c-plane AlGaN on gamma-LiAlO2
作者:	Tun,CJ;Kuo,CH;Fu,YK;Kuo,CW;Chou,MMC;Chi,GC
贡献者:	光電科學研究所
关键词:	2-STEP GROWTH;GAN;SAPPHIRE;GAN(1(1)OVER-BAR-00);LIALO2(100);EPITAXY;ALN
日期:	2009
上传时间:	2010-06-29 19:41:38 (UTC+8)
出版者:	中央大學
摘要:	This study demonstrates a pure c-plane AlGaN epilayer grown on a gamma-LiAlO2 (1 0 0) (LAO) substrate with an AlN nucleation layer grown at a relatively low temperature (LT-AlN) by metal-organic chemical vapor deposition (MOCVD). The AlGaN film forms polycrystalline film with m- and c-plane when the nucleation layer grows at a temperature ranging from 660 to 680 degrees C. However, a pure c-plane AlGaN film with an Al content of approximately 20% can be obtained by increasing the LT-AlN nucleation layer growth temperature to 700 degrees C. This is because the nuclei density of AlN increases as the growth temperature increases, and a higher nuclei density of AlN deposited on LAO substrate helps prevent the deposition of m-plane AlGaN. Therefore, high-quality and crack-free AlGaN films can be obtained with a (0 0 0 2) omega-rocking curve FWHM of 547 arcsec and surface roughness of 0.79 nm (root-mean-square) using a 700-degrees C-grown LT-AlN nucleation layer. (C) 2009 Elsevier B.V. All rights reserved.
關聯:	JOURNAL OF CRYSTAL GROWTH
显示于类别:	[光電科學研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	535	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing