題名:	矽/石英晶圓鍵合之熱壓研究;Investigation of Si/Quartz Wafer Bonding for Hot Press
作者:	薛少宗;Shao-Zong Xiue
貢獻者:	機械工程研究所
關鍵詞:	晶圓鍵合;石英上覆矽;熱壓試驗機;SOQ;hot press;wafer bonding
日期:	2010-07-26
上傳時間:	2010-12-08 13:45:01 (UTC+8)
出版者:	國立中央大學
摘要:	異質材料的晶圓接合技術由於能克服材料本身在磊晶技術上的限制，因而不受限於相異晶格材料，於半導體與光電產業上提供多樣化的複合基板，深具研究發展與商業化價值。其中石英上覆矽(SOQ)晶圓得以應用在微機電系統、平面顯示器、生物醫療等科技領域，但石英與矽晶圓的熱膨脹係數差異甚大，導致接合後加溫同時因熱應力增加造成翹曲、破裂甚至分離，在無法有效退火增加鍵結能的情況下使後續的薄化製程遭受困難。在研究中試圖從熱壓試驗機(Hot Press)的壓力參數調整出有效抑制因熱應力所衍生出膨脹及形變的問題。利用上、下壓板給予矽/石英晶圓對一夾持力與後續升溫所產生之應力抗衡，結果顯示鍵合溫度足以超越200℃並且晶圓對沒有因熱應力產生剝離。 Wafer bonding technology of the dissimilar materials can surmount the material itself in the epitaxy technology which is not limited to the different crystal lattice materials. That can provide the compound substrate of diversification at the semiconductor and the optoelectronics industry, and also have research development and commercial value. Quartz on silicon (SOQ) wafer can apply in the science and technology field, such as MEMS, FPD and biomedicine…etc. Because of the mismatch of the quartz and silicon wafer thermal expansion coefficients (CTE), after the joint, thermal stress will be induced and causes the warp, breakage, even to separate. That makes the bonding pairs unable to increase the bonding energy on the effective annealing process. In this study, we attempts to find out the pressure parameters of the hot press adjustment for effective inhibition of thermal stress generated due to the expansion and deformation problems. The top plate and the bottom plate give the silicon/quartz wafer pair clamping force and following resistance the stress generated by heating. The results show that the bonding temperature can over than 200℃ and the bonding pair wouldn’t be separated by the thermal stress.
顯示於類別:	[機械工程研究所] 博碩士論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	807	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing

資料載入中.....