Abnormal Cu(3)Sn Growth and Kirkendall Formation Between Sn and (111) and (220) Preferred-Orientation Cu Substrates

NCUIR > Engineering College > Department of Chemical and Materials Engineering > journal & Dissertation > Item 987654321/49921

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/49921

Title:	Abnormal Cu(3)Sn Growth and Kirkendall Formation Between Sn and (111) and (220) Preferred-Orientation Cu Substrates
Authors:	Huang,TS;Tseng,HW;Hsiao,YH;Cheng,CH;Lu,CT;Liu,CY
Contributors:	化學工程與材料工程學系
Keywords:	LEAD-FREE SOLDERS;VOID FORMATION;JOINTS;RELIABILITY;EVOLUTION;LAYERS
Date:	2011
Issue Date:	2012-03-27 16:26:31 (UTC+8)
Publisher:	國立中央大學
Abstract:	(111) and (220) preferred-orientation Cu substrates were successfully produced by varying electroplating current-density. While these preferred-orientation Cu substrates reacted with Sn, serious Kirkendall voids formed at the interfaces between Sn and (111) and (220) preferred-orientation Cu substrates. Also, abnormal Cu(3)Sn growth occurs; the Cu(3)Sn layer decreased upon aging and vanished after 1000-h aging. With a prolonged 2000-h aging, a Cu(3)Sn layer re-grew at the Cu(6)Sn(5)/Cu interface. The abnormal Cu(3)Sn growth was found to highly associate with serious Kirkendall formation (C) 2011 The Electrochemical Society. [DOI: 10.1149/1.3608248] All rights reserved.
Relation:	ELECTROCHEMICAL AND SOLID STATE LETTERS
Appears in Collections:	[Department of Chemical and Materials Engineering] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	643	View/Open

社群 sharing