Highly conductive alumina-added ZnO ceramic target prepared by reduction sintering and its effects on the properties of deposited thin films by direct current magnetron sputtering

NCUIR > College of Electrical Engineering & Computer Science > Department of Electrical Engineering > journal & Dissertation > Item 987654321/51957

Please use this identifier to cite or link to this item: http://ir.lib.ncu.edu.tw/handle/987654321/51957

Title:	Highly conductive alumina-added ZnO ceramic target prepared by reduction sintering and its effects on the properties of deposited thin films by direct current magnetron sputtering
Authors:	Huang,HS;Tung,HC;Chiu,CH;Hong,IT;Chen,RZ;Chang,JT;Lin,HK
Contributors:	電機工程學系
Keywords:	AL-DOPED ZNO;ZINC-OXIDE FILMS;ELECTRICAL-PROPERTIES;SOLAR-CELLS;TEMPERATURE
Date:	2010
Issue Date:	2012-03-28 10:11:50 (UTC+8)
Publisher:	國立中央大學
Abstract:	To obtain a suitable sputtering target for depositing transparent conducting Al-doped ZnO (AZO) films by using direct current (DC) magnetron sputtering, this study investigates the possibility of using atmosphere controlled sintering of Al(2)O(3) mixed ZnO powders to prepare highly conductive ceramic AZO targets Experimental results show that a gas mixture of Ar and CO could produce a sintered target with resistivity in the range of 2.23 x 10(-4) Omega cm. The fairly low resistivity was mainly achieved by the formation of both aluminum substitution (Al(Zn)) and oxygen vacancy (V(O)). thus greatly increasing the carrier concentration. Compared to usual air sintered target, the thin film deposited by the Ar + CO sintered target exhibited lower film resistivity and more uniform spatial distribution of resistivity A film resistivity as low as 6.8 x 10(-4) Omega cm was obtained under the sputtering conditions of this study. ((C) 2010 Elsevier B.V. All rights reserved.
Relation:	THIN SOLID FILMS
Appears in Collections:	[Department of Electrical Engineering] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	331	View/Open

社群 sharing

Loading...