Cu/Sn接合系統中銅鍍層晶格優選方向對Kirkendall voids的形成機制探討與研究;Effect of Preferred-Orientation of Electroplated Cu on Kirkendall-Voids Formation at Cu/Sn Joint Interface

NCU Institutional Repository > 工學院 > 化學工程與材料工程學系 > 研究計畫 > Item 987654321/62305

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/62305

题名:	Cu/Sn接合系統中銅鍍層晶格優選方向對Kirkendall voids的形成機制探討與研究;Effect of Preferred-Orientation of Electroplated Cu on Kirkendall-Voids Formation at Cu/Sn Joint Interface
作者:	劉正毓
贡献者:	國立中央大學化學工程與材料工程學系
关键词:	化學工程;材料科技
日期:	2012-12-01
上传时间:	2014-03-17 11:29:27 (UTC+8)
出版者:	行政院國家科學委員會
摘要:	研究期間：10108~10207;Due to the environment concern, Pb-free solder has been wildly used in electronic packaging industry. Yet, the Kirkendall voids at the solder joint interface is a major reason to degrade the reliability of the solder joints. Futhermore, with the shrinkage of the solder joint size, the reaction compound would be the dominant part in the entire solder joint. As the compound forms intensively in the micro solder joint, Kirkendall voids likely form at the interface. Therefore, Kirkendall voids at the solder joint play a critical role for the reliability of the solder joints. Take 3D IC TSV packaging as an example, the electroplate Cu via should be joined by thin Sn-based solder layer. Large amount of Cu-Sn compound formed at the solder joint interface, which results the formation of Kirkendall voids. Thus, the reliability of the solder joint is no longer depends on the solder joint materials only but it might be dominated by the formation of Kirkendall voids. Besides, the microstructure (texture orientation) of the electroplate Cu TSV is very critical to the formation of Kirkendall voids. So far, the relation between Cu-Sn joint strength and the formation of Kirkendall voids has not been studied systematically. The purpose of this project is to investigate and model relationship between the Cu-Sn joint reliability and the Kirkendall voids. In this proposed three-years project, we will investigate the effect of Cu preferred-orientation ((111),(220),(200),(Random)) on Kirkendall voids formation at the Cu/Sn joint interface. Three major approaches in this research: (1) physical property of different preferred-orientation electroplated Cu. (2) under thermal aging and electromigration, the effect of the Cu preferred-orientation on Kirkendall voids formation at the Cu/Sn joint interface. (3) under thermal aging and electromigration, the relationship between Kirkendall voids coverage and the solder joint strength.
關聯:	財團法人國家實驗研究院科技政策研究與資訊中心