摘要(英) |
TaON, TaON-Ag, TaON-(Ag,Cu) were prepared by reactive co-sputtering of Ta, Ag and Cu in O2, N2, and Ar plasma. The deposition temperature was 300 °C. The Ag contents in TaON-Ag were 2 at.%, 5 at.%, 7 at.%, 10 at.% and the Ag-Cu contents in TaON-(Ag,Cu) were 1.5 at.% - 1.5 at.%, 2.5 at.% - 2.5 at.%, 5 at.% - 5 at.%, 3 at.% - 7 at.%, 7 at.% - 3 at.% respectively. After deposition, all the samples were annealed at 800 °C for 5 minutes by rapid thermal annealing (RTA). These films were characterized by a variety of techniques including X-ray diffraction, FESEM (field emission scanning electron microscopy), and TEM (transmission electron microscopy). Inductively coupled plasma optical emission spectrometer (ICP-OES) was used to analyze dissolved ion concentrations when the thin films were immersed in the buffer solution. The antibacterial tests were carried out with E-coli. The results show that the un-doped TaON could be used as a visible-light antibacterial photo-catalyst. TaON–Ag films, with or without visible light irradiation, have a significantly improvement in antibacterial behavior. Furthermore, it is found that co-deposition of Ag and Cu into TaON films could lead to a triple bactericidal effect, due to the antibacterial effects of Ag, Cu, and TaON.
At final, antibacterial kinetics was used to analyze the bactericidal effects of these TaON thin films doped with Ag and Ag-Cu with various concentrations. The results confirm that TaON-( Ag, Cu) films have a triple effect on antibacterial efficiency. To further understand the synergistic effect of Ag and Cu ions on bactericidal behaviors, kinetic analyses were also carried out on Ag and/or Cu ions- containing buffer solution, the solution that contained both ions showed much improved antibacterial behaviors, compared with that contained only Ag or Cu ions |
參考文獻 |
【1】T. Riekkinen , J. Molarius etc., “Reactive sputter deposition and properties of TaN thin films” Microelectronic Engineering 64 (2002) 289–297
【2】O. Banakh , T. Heulin and P. E. Schmid etc., “Influence of process parameters on the properties of the tantalum oxynitride thin films deposited by pulsing reactive gas sputtering” J. Vac. Sci. Technol. Mar/Apr 2006
【3】J.H. Hsieh , C.C. Chang , etc., “Optical properties and hydrophilic behaviors of TaOxNy thin films with and without rapid thermal annealing” Thin Solid Films 517 (2009) 4711–4714
【4】S. Venkataraj , H. Kittur , etc., “Multi-technique characterization of tantalum oxynitride films prepared by reactive direct current magnetron sputtering” Thin Solid Films 514 (2006) 1 – 9
【5】M. Ohring, The Materials Science of Thin Films, Academic Press, San Diego, 1991.
【6】S. Venkataraj, D. Severin, , etc., “Towards understanding the superior properties of transition metal oxynitrides prepared by reactive DC magnetron sputtering” Thin Solid Films 502 (2006) 228 – 234
【7】T. TAKATA1, G. HITOKI, etc., “Visible-light-driven photocatalytic behavior of tantalum-oxynitride and nitride” Res. Chem. Intermed., Vol. 33, No. 1–2, pp. 13–25 (2007)
【8】Go Hitoki, Tsuyoshi Takata, etc., “An oxynitride, TaON, as an efficient water oxidation photocatalyst under visible light irradiation (l 5 500 nm)” Res. Chem. Intermed., CHEM. COMMUN. , 2002, 1698–1699
【9】Sung-Lae Cho, Byung-Sung Kim, etc., “Metallorganic Chemical Vapor Deposition of TaOxNy as a High-Dielectric-Constant Material for Next-Generation Devices” Res. Chem. Intermed., J. Electrochem. Soc. 2002, Volume 149, Issue 10, Pages C529-C537
【10】Kazuhito Hashimoto, Hiroshi Irie, etc., “TiO2 Photocatalysis: A Historical Overview and Future Prospects” AAPPS Bulletin December 2007, Vol. 17, No. 6
【11】Kristopher Page,Robert G. Palgrave, etc., “Titania and silver–titania composite films on glass—potent antimicrobial coatings” J. Mater. Chem., 2007, 17, 95–104
【12】Caixia Sun, Qi Li, etc., “Enhanced Photocatalytic Disinfection of Escherichia coli Bacteria by Silver Modification of Nitrogen-Doped Titanium Oxide Nanoparticle
Photocatalyst Under Visible-Light Illumination” J. Am. Ceram. Soc., 93 [11] 3880–3885 (2010)
【13】Sambandam Anandan, Nalenthiran Pugazhenthiran, etc., “Investigation on photocatalytic potential of Au–Ta2O5 semiconductor nanoparticle by degrading Methyl Orange in aqueous solution by illuminating with visible light” Catal. Sci. Technol., 2012, 2, 2502–2507
【14】Kayanosunada , Toshiyawatanabe, etc., “Bactericidal Activity of Copper Deposited TiO2 Thin Film under Weak UV Light Illumination” Environ. Sci. Technol. 2003, 37, 4785-4789
【15】Steven N. Frank, Allen J. Bard, etc., “Heterogeneous Photocatalytic Oxidation of Cyanide Ion in Aqueous Solutions at Ti02 Powder” Journal of the American Chemical Society 1 99:l / January 5, 1977
【16】Joe H. Hsieh., “Semiconductor Nanocomposite Films for Clean Environment” 93932_C004.indd p129-p154
【17】金宗哲,“無機抗菌材料及應用”,化學工業出版社, P26, (2004)
【18】張哲誠, “以濺鍍法製備氮氧化鉭-銀複合薄膜及其特性之研究”,明志科技大學碩士論文
【19】Ivan Sondi and Branka Salopek-Sondi., “Silver nanoparticles as
antimicrobial agent: a case study on E. coli as a model for
Gram-negative bacteria” Journal of Colloid and Interface Science 275
(2004) 177–182
【20】Peter K. Stoimenov, Rosalyn L. Klinger etc., “Metal Oxide
Nanoparticles as Bactericidal Agents” 2002 American Chemical
Society, 18, 6679-6686
【21】季軍暉、史維明,”抗菌材料”, 學工業出版社 P46 , (2004)
【22】金宗哲, “無機抗菌材料及應用”, 化學工業出版社, P37, (2005)
【23】平松實、福崎智司,”The Antibacterial Activity of Plated Coatings”, 表
面技術,vol.52,No1,PP.58,(2001)
【24】小林道雄, “Antibacterial Metal Surface Treatment”,表面技術, 第49
期,P.43
【25】鍾楊聰等譯, ,”微生物學 第四版”P192, 偉明圖書有限公司
【26】ERIC J. RENTZ DO COMM CNMO, “Viral Pathogens and Severe
Acute Respiratory Syndrome: Oligodynamic Ag+ for Direct Immune
Intervention” Journal of Nutritional & Environmental Medicine (June
2003) 13(2), 109–118
【27】C. W. HIATT, “KINETICS OF THE INACTIVATION OF VIRUSES” American Society for Microbiology Printed in U.S.A. BAC’rERIOLOGICAL REVIEWS Vol. 28, No. 2, pp. 150-163 June, 1964
【28】H.mattie “kinetics of antimicrobial action” Review of infections diseases.vol.3.No.1.January.february
【29】SVEN GARD., “CHEMICAL INACTIVATION OF VIRUSES” The Nature of’ Viruses P 123-P146
【30】YU-SEN E. LIN, RADISAV D. VIDIC, etc., “INACTIVATION OF MYCOBACTERIUM AVIUM BY COPPER AND SILVER IONS” Wat. Res. Vol. 32, No. 7, pp. 1997±2000, 1998
【31】YU-SEN E. LIN , RADISAV D. VIDIC, etc., “INDIVIDUAL AND COMBINED EFFECTS OF COPPER AND SILVER IONS ON INACTIVATION OF LEGIONELLA PNEUMOPHILA” Wat. Res. Vol. 30, No. 8, pp. 1905-1913, 1996
【32】Hsin-I Huang, Hsiu-Yun Shih, etc., “In vitro efficacy of copper and silver ions in eradicating Pseudomonas aeruginosa, Stenotrophomonas maltophilia and Acinetobacter baumannii: Implications for on-site disinfection for hospital infection control” WAT E R RE S E ARCH 42 ( 2008 ) 73 – 80
【33】柯文賢, “表面與薄膜處理技術”,P8-17~P8-18 全華科技
【34】陳力俊,“材料電子顯微鏡學”,P34 國科會精儀中心
【35】J.H. Hsieh, C.C. Chang, etc., “Effects of Ag contents on antibacterial behaviors of TaON–Ag nanocomposite thin films” Surface & Coatings Technology 205 (2010) S337–S340
【36】汪建民主編,“材料分析”,P34 中國材料科學學會
【37】C.M. Wang , J.H. Hsieh, etc., “Electrical properties of TaN–Cu nanocomposite thin films” Ceramics International 30 (2004) 1879–1883
【38】J. Musil, J. Vlˇcek, “Magnetron sputtering of hard nanocomposite coatings and their properties” Surface and Coatings Technology 142_144 Ž2001. 557_566
【39】柯賢文,”腐蝕與防蝕”, P42台北全華科技股份有限公司 |