dc.description.abstract | 摘 要
在微細加工的領域中,微細放電加工法可有效地用來製造孔徑小於100μm的微細孔,但以微細放電加工法在金屬板上製作微細孔時,因孔壁的表面會形成再鑄層,其包含了微裂痕與放電坑等缺陷,孔壁表面粗度不佳,嚴重影響微細孔的品質。
因此,本研究擬以高鎳合金為工件材料,結合微細放電與電解拋光兩種加工法,進行微細孔加工,期能改善在放電後的高鎳合金微細孔的孔壁表面品質,使其符合精密工業的需求。
由實驗結果顯示,採用電解拋光法加工微細孔時,孔壁表面可獲得顯著的拋光效果。以放電電流500mA加工後的微細孔為例,在輸入電解電壓2V、電極不轉動、電解液濃度比例1:10、電解液不流動、加工時間約5分鐘時,即可獲得孔壁表面平整光滑的微細孔。此法亦可應用於各式微細異形孔的孔壁表面之改善。 | zh_TW |
dc.description.abstract | Abstract
Micro-holes with diameter less than 100μm can be effectively fabricate by micro-EDM in micro-machining. But using micro-EDM to manufacture micro-holes on metal plate, the recast layer include micro-crack and crater was formed on the hole-wall will lead to poor surface roughness to affect quality of micro-hole seriously.
For this reason, the Hymu-80 was chosen as the workpiece material in this study, using micro-EDM combined with electropolishing to machine micro-holes. It expected to improve the quality of micro-holes after EDM to satisfy the precision engineering. The results showed that, using electropolishing to machine the surface of the hole-wall could obtain obviously improvement. | en_US |
DC.subject | 微細放電加工 | zh_TW |
DC.subject | 高鎳合金 | zh_TW |
DC.subject | 電解拋光 | zh_TW |
DC.subject | 線放電研磨 | zh_TW |
DC.subject | 微細孔 | zh_TW |
DC.subject | WEDG | en_US |
DC.subject | EP | en_US |
DC.subject | micro-holes | en_US |
DC.subject | Hymu | en_US |
DC.subject | Micro-EDM | en_US |
DC.title | 結合微細放電與電解拋光之微孔加工研究 | zh_TW |
dc.language.iso | zh-TW | zh-TW |
DC.title | Study of Micro-holes Machining Using Micro-EDM Combined with Electropolishing | en_US |
DC.type | 博碩士論文 | zh_TW |
DC.type | thesis | en_US |
DC.publisher | National Central University | en_US |