We demonstrated a unique approach to generate self-organized, self-alignment, and low-cost Ge-nanoball/SiO2/SiGe-shell gate-stacking heterostructures through the selective oxidation of poly-Si0.83Ge0.17 nano-pillars over the Si3N4 buffer layer on the Si substrate, and then would like to realize SiGe MOSFETs based on this designer heterostructure in the near future. It has been previously demonstrated that the interface trap density (Dit) of SiO2/SiGe heterostructure in the designer heterostructure is about 3.5−5.5 × 1011 cm-2eV-1, which is a promising candidate for high-performance Ge MOSFETs. However, 4nm-thick amorphous interfacial oxide layer was generated during thermal oxidation at 900 °C in H2O ambient, which cannot meet the criteria of prevailing CMOS technology with gate oxide less than 1 nm. In this work, we further reduced the thickness of this SiO2 interfacial layer by tuning the oxidation conditions, such as temperature and oxidation ambient. On the other hand, a SOI substrate was also employed to decrease the SiGe-shell thickness and then increase the Ge content in SiGe shell, forming a high-carrier mobility channel.
According to a series of experiments with various oxygen fluxes and temperatures in thermal oxidation process as well as different Si substrate to control Si flux, we found the thickness of interfacial SiO2 layer would be significantly reduced with decreasing thermal oxidation/annealing temperature. Meanwhile, gate-oxide quality was also raised as the oxidation temperature decreased, which was confirmed by extensive current-voltage and capacitance-voltage characterizations in MOSC devices. Both results provide great promises for apply the designer gate-stacking heterostructure in Ge MOS applications.
|
參考文獻 |
參考文獻
[1] T. Ghani et al., “A 90nm high volume manufacturing logic technology featuring novel 45nm gate length strained silicon CMOS transistors,” IEDM Tech. Dig., p. 11.6.1, 2003.
[2] D. Kuzum, “Interface-engineered Ge MOSFETs for future high performance CMOS applications,” dissertation for the degree of doctor, Stanford university, 2009.
[3] D. Kuzum et al., “Ge Interface Engineering with Ozone Oxidation for Low Interface State Density,” IEEE Elec. Dev. Lett., vol. 29, p. 328, 2008.
[4] P. Zimmerman, G. Nicholas, B. De Jaeger, B. Kaczer, A. Stesmans, L. A. Ragnarsson, D. P. Brunco, F. E. Leys, M. Caymax, G. Winderickx, K. Opsomer, M. Meuris, and M. M. Heyns, “High performance Ge pMOS devices using a Si-compatible process flow,” Tech. Dig. Int. Electron Devices Meets., 655 (2006).
[5] Y. Nakakita, R. Nakane, T. Sasada, H. Matsubara, M. Takenaka, and S. Takagi, “Interface-controlled self-align source/drain Ge pMOSFETs using thermally-oxidized GeO2 interfacial layers,” Tech. Dig. Int. Electron Devices Meets., 877 (2008).
[6] 楊國慶,“自組式鍺奈米球/二氧化矽/矽鍺合金閘堆疊異質結構之介面工程最佳化探討”,碩士論文,國立中央大學,民國103年。
[7] C. Y. Chien et al., “Nanoscale, catalytically enhanced local oxidation of silicon-containing layers by ‘burrowing’ Ge quantum dots,” Nanotechnology, vol. 22, p. 435602, 2011.
[8] M. H. Kuo et al., “Designer Ge quantum dots on Si: A heterostructure configuration with enhanced optoelectronic performance,” Appl. Phys. Lett., vol. 101, p. 223107, 2012.
[9] K. H. Chen, C. C. Wang, T. George, and P. W. Li “The pivotal role of SiO formation in the migration and Ostwald ripening of Ge quantum dots,” Appl. Phys. 105, 122102 (2014)
[10] Nishimura T, Lee CH, Tabata T, Wang SK, Nagashio K, Kita K, et al. High-electronmobility Ge n-channel metal-oxide-semiconductor field-effect transistors with high-pressure oxidized Y2O3. Appl Phys Express. 2011;4:064201.
[11] Zhang R, Iwasaki T, Taoka N, Takenaka M, Takagi S. High-mobility Ge pMOSFET with 1-nm EOT A2O3/GeOx/Ge gate stack fabricated by plasma post oxidation. IEEE Trans Electron Devices. 2012;59:335–41.
[12] Lee CH, Nishimura T, Nagashio K, Kita K, Toriumi A. High-electron-mobility Ge/GeO2 n-MOSFETs with two-step oxidation. IEEE Trans Electron Devices. 2011;58:1295–301.
[13] Takenaka M, Zhang R, Takagi S. MOS interface engineering for highmobility Ge CMOS. Proc IEEE Int Reliabil Phys Symposium. 2013;4C(1):1–8. Anaheim, 14–18 April.
|