| 題名: | Some observations on the synthesis of fully-dispersible nanocrystalline zeolite ZSM-5 |
| 作者: | 蔣孝澈;Selvin, Rosilda;Chiang, Anthony S. T. |
| 貢獻者: | 工學院化學工程與材料工程學系 |
| 關鍵詞: | Agglomeration;Aging;Aluminum;Heating;Nanocrystals;Nanoparticles - chemistry;Nanostructure;Nanotechnology;Particle Size;Synthesis;Zeolites;Zeolites - chemistry |
| 日期: | 2014-09-01 |
| 上傳時間: | 2026-04-21 14:27:45 (UTC+8) |
| 出版者: | American Scientific Publishers;26650 The Old Road, Suite 208, Valencia, California 91381-0751, USA: American Scientific Publishers |
| 摘要: | 摘要： A facile method for the rapid synthesis of fully-dispersible ZSM-5 (Si/Al = 100) of about 30 nm size in high yield (about 91%) is described. The method comprises three steps, viz., concentration of an initial clear solution, low-temperature (80 °C) ageing of concentrated sol, and high-temperature (175 °C) hydrothermal treatment or microwave heating (175 °C) of aged concentrated sol. A simple vacuum-concentration method was used for the extraction of pure NPs of ZSM-5 in solution. XRD, FT-IR, TGA and ASAP characterizations showed that the NPs were partially crystalline. The concentration step accelerated the aggregation of primary units, which helps in the production of a large number of nucleation centers protected by TPA+ ions against aggregation. During low-temperature ageing, the number of critical sized nuclei increases, growing into zeolite. The high-temperature heating results in the complete growth of unreacted silica, giving high yields. A key factor for generating small non-aggregated zeolite crystals is the amount of water in the synthesis sol. The three-step method presented here produces a target material of small and uniform sized, non-aggregated ZSM-5 of about 30 nm in a short reaction time. The results are significant, as the synthesis method adopted here produces much uniform, non-aggregated nanocrystalline ZSM-5 in a shorter time with high yield.
其他題名： J Nanosci Nanotechnol
出版者： 26650 The Old Road, Suite 208, Valencia, California 91381-0751, USA: American Scientific Publishers
出版日期： 2014-09-01
出處： Journal of nanoscience and nanotechnology, 2014-09, Vol.14 (9), p.7351-7359
識別號： ISSN: 1533-4880
識別號： EISSN: 1533-4899
識別號： DOI: 10.1166/jnn.2014.9239
識別號： PMID: 25924414 |
| 顯示於類別: | [化學工程與材料工程學系 ] 期刊論文
|
文件中的檔案:
| 檔案 |
描述 |
大小 | 格式 | 瀏覽次數 |
|---|
| index.html | | 0Kb | HTML | 13 | 檢視/開啟 |
|
在NCUIR中所有的資料項目都受到原著作權保護.
|