Unraveling the high performance of tri-iodide perovskite absorber based photovoltaics with a non-polar solvent washing treatment

Please use this identifier to cite or link to this item: https://ir.lib.ncu.edu.tw/handle/987654321/101532

Title:	Unraveling the high performance of tri-iodide perovskite absorber based photovoltaics with a non-polar solvent washing treatment
Authors:	吳春桂;Lin, Kuen-Feng;Chang, Sheng Hsiung;Wang, Kai-Hung;Cheng, Hsin-Ming;Chiu, Kuo Yuan;Lee, Kun-Mu;Chen, Sheng-Hui;Wu, Chun-Guey
Contributors:	理學院化學學系
Keywords:	2D XRD;Crystallinity;Excitation;Perovskites;Photoluminescence;Photovoltaic cells;Photovoltaics;Solar cells;Toluene;Tri-iodide perovskite film;Washing
Date:	2015-06-23
Issue Date:	2026-04-21 14:37:11 (UTC+8)
Publisher:	Elsevier BV;Elsevier B.V
Abstract:	摘要： A comprehensive study was carried out to understand the formation of a crystalline tri-iodide perovskite absorber (TPA) on top of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS). Scanning electron microscopy, two-dimensional X-ray diffraction and nanosecond time-resolved photoluminescence were used to explore the correlation between the surface morphology and the exciton lifetime in TPA fabricated with and without the in-situ toluene washing treatment. The toluene washing treatment decreases the crystallinity (exciton lifetime) of TPA and improves the TPA coverage on the non-crystalline PEDOT:PSS surface. The high average power conversion efficiency (PCE) of 10.61% achieved can be explained as due to the efficient exciton dissociation at the interface between the TPA and the PEDOT:PSS. The experimental results show that the PCE can be further improved when the crystallinity of TPA and the TPA coverage on PEDOT:PSS are simultaneously optimized. •The correlation between morphology and crystallization of perovskite film is studied.•A high average power conversion efficiency of 10.61% was achieved.•PL data shows that excitons efficiently dissociate at perovskite–PEDOT interfaces. 出版者： Elsevier B.V 出版日期： 2015-10-01 出處： Solar energy materials and solar cells, 2015-10, Vol.141, p.309-314 資源來源： Elsevier ScienceDirect Journals Complete - Autoholdings 版權： 2015 Elsevier B.V. 識別號： ISSN: 0927-0248 識別號： EISSN: 1879-3398 識別號： DOI: 10.1016/j.solmat.2015.06.002