Carbon nanotube-supported Cu3N nanocrystals as a highly active catalyst for oxygen reduction reaction

NCU Institutional Repository > 工學院 > 材料科學與工程研究所 > 期刊論文 > Item 987654321/103385

請使用永久網址來引用或連結此文件: https://ir.lib.ncu.edu.tw/handle/987654321/103385

題名:	Carbon nanotube-supported Cu3N nanocrystals as a highly active catalyst for oxygen reduction reaction
作者:	王冠文;Su, C.-Y;Liu, B.-H;Lin, T.-J;Chi, Y.-M;Kei, C.-C;Wang, K.-W;Perng, T.-P
貢獻者:	工學院材料科學與工程研究所
日期:	2015-08-07
上傳時間:	2026-04-23 11:29:26 (UTC+8)
出版者:	Royal Society of Chemistry
摘要:	摘要： A controllable synthesis of a hybrid electrocatalyst consisting of copper( i ) nitride nanoparticles (Cu 3 N) grown on carbon nanotubes (CNTs) by plasma enhanced atomic layer deposition (ALD) is presented. The island growth mechanism during ALD led to the formation of uniformly distributed Cu 3 N nanoparticles on the surface of CNTs. The size of copper nitride particles strongly influenced the electrocatalytic properties, and it could be precisely tuned by controlling the cycle number of ALD. The Pt-free non-precious nanocrystals coupling with CNTs exhibited pronounced electrocatalytic activity for oxygen reduction reaction (ORR). Koutecky-Levich analysis on the ORR current densities indicated that the Cu 3 NCNT electrodes in alkaline media follow a mixed two- and four-electron transfer ORR pathway, whose mass activities are comparable to that of a typical Pt/C electrode. This report reveals a dry process to fabricate a well-dispersed metal nitride on a selected support material as an ORR catalyst that could enhance the catalytic activity by synergistic chemical coupling effects. We report a heterostructured Cu 3 NCNT electrocatalyst for application in alkaline fuel cells. The size of well-dispersed Cu 3 N nanoparticles can be precisely controlled by ALD. Superior catalytic oxygen reduction reaction performance was achieved with a mixed two- and four-electron process. 出版日期： 2015-09-15 資源來源： Royal Society of Chemistry 識別號： ISSN: 2050-7488 識別號： EISSN: 2050-7496 識別號： DOI: 10.1039/c5ta04383b
顯示於類別:	[材料科學與工程研究所 ] 期刊論文