Fabrication of orderly copper particle arrays on a multi-electrolyte-step anodic aluminum oxide template

NCU Institutional Repository > 理學院 > 光電科學與工程學系 > 期刊論文 > Item 987654321/103408

請使用永久網址來引用或連結此文件: https://ir.lib.ncu.edu.tw/handle/987654321/103408

題名:	Fabrication of orderly copper particle arrays on a multi-electrolyte-step anodic aluminum oxide template
作者:	陳昇暉;Chen, Sheng-Hui;Lee, Cheng-Chung;Chan, Der-Sheng;Chen, Chun-Ko
貢獻者:	理學院光電科學與工程學系
關鍵詞:	Acids;Aluminum;Aluminum oxide;Arrays;Bias;Circularity;Copper;Electric potential;Nanocomposites;Nanomaterials;Nanoparticles;Nanostructure;Quantum dots;Standard deviation
日期:	2013-12-01
上傳時間:	2026-04-23 11:29:55 (UTC+8)
出版者:	Hindawi Publishing Corporation;Cairo, Egypt: Hindawi Limiteds
摘要:	摘要： A multi-electrolyte-step (MES) anodic aluminum oxide (AAO) method was used to achieve nanochannel arrays with good circularity and periodic structure. The nano-channel array fabrication process included immersion in a phosphoric acid solution with a 120–150 bias voltage. Bowl-shaped structures were then formed by removing the walls of the nano-channel arrays. The nano-channel arrays were grown from the bottom of the bowl structure in an oxalic solution using a 50 V bias voltage. A comparison of this new MES process with the one-step and five-step AAO process showed a 50% improvement in the circularity over the one-step process. The standard deviation of the average period in the MES array was 25 nm which is less than that of one-step process. This MES method also took 1/4 of the growing time of the five-step process. The orderliness of the nano-channel arrays for the five-step and MES process was similar. Finally, Cu nanoparticle arrays with a 200 nm period were grown using an electroplating process inside the MES nano-channel arrays on fluorine doped tin oxide glass. Stronger surface plasmon resonance absorption from 550 nm to 750 nm was achieved with the MES process than was possible with the one-step process. 出版者： Cairo, Egypt: Hindawi Limiteds 出版日期： 2013-01-01 出處： Journal of Nanomaterials, 2013-01, Vol.2013 (2013), p.485-491-453 資源來源： Airitilibrary華藝線上圖書館版權： Copyright © 2013 Chun-Ko Chen et al. 版權： Copyright © 2013 Chun-Ko Chen et al. Chun-Ko Chen et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited. 識別號： ISSN: 1687-4110 識別號： ISSN: 1687-4129 識別號： EISSN: 1687-4129 識別號： DOI: 10.1155/2013/784927