Effects of annealing temperature on stress corrosion susceptibility of AA5083-H15 alloys

NCU Institutional Repository > 工學院 > 材料科學與工程研究所 > 期刊論文 > Item 987654321/103525

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://ir.lib.ncu.edu.tw/handle/987654321/103525

题名:	Effects of annealing temperature on stress corrosion susceptibility of AA5083-H15 alloys
作者:	李勝隆;Yen, Chun-Hung;Wu, Chih-Ting;Chen, Yen-Hao;Lee, Sheng-Long
贡献者:	工學院材料科學與工程研究所
关键词:	Alloys;Aluminum alloys;Aluminum base alloys;Analysis;Annealing;Applied and Technical Physics;Biomaterials;Cold;Corrosion;Corrosion resistance;Elongation;Energy;Grain boundaries;Inorganic Chemistry;Intergranular corrosion;Materials Engineering;Materials research;Materials Science;Metal forming;Microscopy;Microstructure;Nanotechnology;Nitric acid;Slow strain rate;Stress corrosion;Stress corrosion cracking;Stress state;Studies;Temperature;Tension tests
日期:	2016-04-28
上传时间:	2026-04-23 11:32:11 (UTC+8)
出版者:	Cambridge University Press;New York, USA: Cambridge University Press
摘要:	摘要： Effects of annealing temperature on stress corrosion susceptibility of AA5083–H15 alloys were studied by annealing specimens at 150, 200, 250, 300, and 350 °C before sensitization. Nitric acid mass loss testing and slow strain rate testing were conducted to investigate intergranular corrosion (IGC) and stress corrosion cracking (SCC). Results indicate that H15 alloy was less susceptible to IGC, but this alloy had the highest susceptibility to IGC and SCC after sensitization. Due to the continuous precipitation of β phase, the sensitized 150 and 200 °C alloys were highly susceptible to IGC and SCC. The 250 °C alloy was less susceptible to IGC because of the absence of the precipitation of β phase. After sensitization, this alloy was also less susceptible to IGC and SCC on account of the discontinuous precipitation of β phase. The sensitized 300 and 350 °C alloys were susceptible to IGC but less susceptible to SCC because of their lower strength and higher elongation. 其他題名： Journal of Materials Research 其他題名： J. Mater. Res 出版者： New York, USA: Cambridge University Press 出版日期： 2016-04-28 出處： Journal of materials research, 2016-04, Vol.31 (8), p.1163-1170 資源來源： ABI/INFORM Collection 版權： Copyright © Materials Research Society 2016 版權： The Materials Research Society 2016 識別號： ISSN: 0884-2914 識別號： EISSN: 2044-5326 識別號： DOI: 10.1557/jmr.2016.120 識別號： CODEN: JMREEE