Effects of scandium addition on iron-bearing phases and tensile properties of Al-7Si-0.6Mg alloys

NCUIR > Engineering College > Institute of Materials Science and Engineering > journal & Dissertation > Item 987654321/103550

Please use this identifier to cite or link to this item: https://ir.lib.ncu.edu.tw/handle/987654321/103550

Title:	Effects of scandium addition on iron-bearing phases and tensile properties of Al-7Si-0.6Mg alloys
Authors:	李勝隆;Tzeng, Yu-Chih;Wu, Chih-Ting;Bor, Hui-Yun;Horng, Jain-Long;Tsai, Mu-Lin;Lee, Sheng-Long
Contributors:	工學院材料科學與工程研究所
Keywords:	Al–7Si–0.6Mg alloys;Applied sciences;Cross-disciplinary physics: materials science;rheology;Ductility;Elasticity and anelasticity;Elasticity. Plasticity;Exact sciences and technology;Hardness;Interdendritic shrinkage;Materials science;Mechanical properties and methods of testing. Rheology. Fracture mechanics. Tribology;Metals. Metallurgy;Phase diagrams and microstructures developed by solidification and solid-solid phase transformations;Physics;Scandium;Solidification;Treatment of materials and its effects on microstructure and properties
Date:	2014-01-21
Issue Date:	2026-04-23 11:32:39 (UTC+8)
Publisher:	Elsevier BV;Kidlington: Elsevier B.V
Abstract:	摘要： Iron is the most deleterious impurity in aluminum alloys and can easily combine with aluminum to form an acicular β-Al5FeSi phase that reduces ductility during the solidification of the molten metal. Adding scandium (Sc) to Al–7Si–0.6Mg alloys can transform the acicular β-Al5FeSi phase into a comparatively harmless nodular Sc–Fe phase (Al12Si6Fe2(Mg,Sc)5). This Sc–Fe phase has a lower hardness and elastic modulus than the β-Al5FeSi phase; it is thus less likely to initiate cracks in the Al matrix. Moreover, the nodular Sc–Fe phase can improve the fluidity of Al during solidification, reducing interdendritic shrinkage. Tensile testing measurements showed that the elongation of Al–7Si–0.6Mg alloys with 0.04 and 0.12wt% Sc can be respectively increased by 115% and 110% compared to Al–7Si–0.6Mg without Sc. The corresponding quality indices are increased by 17% and 19%, respectively, suggesting that the tensile properties of Al–7Si–0.6Mg alloys can be enhanced by adding scandium. 出版者： Kidlington: Elsevier B.V 出版日期： 2014-01 出處： Materials Science and Engineering: A, 2014-01, Vol.593, p.103-110 版權： 2013 Elsevier B.V. 版權： 2015 INIST-CNRS 識別號： ISSN: 0921-5093 識別號： EISSN: 1873-4936 識別號： DOI: 10.1016/j.msea.2013.11.039
Appears in Collections:	[Institute of Materials Science and Engineering] journal & Dissertation

Files in This Item:

File	Description	Size	Format
index.html		0Kb	HTML	12	View/Open

社群 sharing

Loading...