摘要： Al–Si alloy often exposed to unfavorable environment such as rain or seawater when they were utilized. The synergistic attack such as wear and corrosion can result in a higher rate of material removal. In the Al–7Si–0.3Mg (A356) alloy, the properties were influenced by the characteristic of eutectic Si particles as well as by the precipitate phase that occurs upon heat treatment. Microstructural changes caused by Sr modifier and subsequent heat treatment as well as the corresponding changes in wear-corrosion property of A356 alloy were studied. The results showed that the addition of Sr modifier changed the morphology of eutectic Si particles and further improved the wear and wear-corrosion properties. Compared to unmodified A356 alloy, the corrosion resistance decreased with addition of Sr. The deterioration in corrosion property triggered the reduction in improvement of wear-corrosion rate when the applied potential increased. The heat treatment of A356 alloy spheroidized and coarsened eutectic Si particles after the solution treatment, strengthened α-Al matrix after the aging treatment. The enhanced microstructure reduced the wear rate and improved the corrosion susceptibility of modified A356 alloy, which further enhanced the wear-corrosion resistance. ► Sr and heat treatment both enhanced the wear-corrosion resistance of A356 alloy. ► Microstructural change from addition of Sr reduced surface crack and material loss. ► Heat treatment reinforced α-Al and corrosion resistance, resulted in limited damage. ► Improvement from heat treatment is higher than that only caused by addition of Sr. 出版者： Elsevier B.V 出版日期： 2012-08-15 出處： Materials chemistry and physics, 2012-08, Vol.135 (2-3), p.503-509 版權： 2012 Elsevier B.V. 識別號： ISSN: 0254-0584 識別號： EISSN: 1879-3312 識別號： DOI: 10.1016/j.matchemphys.2012.05.015