The effect of trace Sc on the quench sensitivity of AL-7Si-0.6 Mg alloys

NCU Institutional Repository > 工學院 > 材料科學與工程研究所 > 期刊論文 > Item 987654321/104284

請使用永久網址來引用或連結此文件: https://ir.lib.ncu.edu.tw/handle/987654321/104284

題名:	The effect of trace Sc on the quench sensitivity of AL-7Si-0.6 Mg alloys
作者:	李勝隆;Tzeng, Yu-Chih;Wu, Chih-Ting;Lee, Sheng-Long
貢獻者:	工學院材料科學與工程研究所
關鍵詞:	Aging (metallurgy);Al3Sc;Aluminum base alloys;Cast;Intermetallic compounds;Magnesium base alloys;Magnesium compounds;Metals and alloys;Microstructure;Precipitates;Precipitation;Quenching;Scandium;Silicides
日期:	2015-12-15
上傳時間:	2026-04-23 11:47:18 (UTC+8)
出版者:	Elsevier;Elsevier B.V
摘要:	摘要： The Jominy end quench test has been adopted to investigate the effect of trace scandium on the quench sensitivity of Al–7Si–0.6 Mg alloys. The results show that at a lower quenching rate, the preferred precipitation of the Al3Sc phase inhibits the formation of a β′-Mg2Si phase, promoting the nucleation of finely dispersed metastable Mg2Si precipitates in the subsequent aging treatment. The quench sensitivity of the Al–7Si–0.6 Mg alloy was effectively improved by more than 60%. Rapid quenching rates can cause the Al matrix of the alloy to be in a supersaturated state, resulting in enhanced mechanical properties after aging treatment. In contrast, slow quenching rates precipitate the relatively coarse β′-Mg2Si phase and also produce a precipitate free zone during the quenching process, thereby diminishing the mechanical properties of the alloy after the aging treatment, so that the Al–7Si–0.6 Mg alloy possesses higher quench sensitivity. •Slow quenching rate led to formation of coarse phases and precipitate free zones.•Al3Sc phases play a vital role in retarding the formation of coarse precipitates.•Adding Sc to Al–7Si–0.6 Mg alloys can improve quench sensitivity. 出版者： Elsevier B.V 出版日期： 2015-12-15 出處： Materials Letters, 2015-12, Vol.161, p.340-342 資源來源： Elsevier ScienceDirect Journals Complete 版權： 2015 Elsevier B.V. 識別號： ISSN: 0167-577X 識別號： EISSN: 1873-4979 識別號： DOI: 10.1016/j.matlet.2015.08.108