Viscous flow and thermoplastic forming ability of a Zr-based bulk metallic glass composite with Ta dispersoids

NCUIR > Engineering College > Institute of Materials Science and Engineering > journal & Dissertation > Item 987654321/104386

Please use this identifier to cite or link to this item: https://ir.lib.ncu.edu.tw/handle/987654321/104386

Title:	Viscous flow and thermoplastic forming ability of a Zr-based bulk metallic glass composite with Ta dispersoids
Authors:	鄭憲清;Li, J.B.;Zhang, H.Z.;Jang, J.S.C.;Jian, S.R.;Li, C.;Huang, J.C.;Nieh, T.G.
Contributors:	工學院材料科學與工程研究所
Keywords:	Amorphous materials;Applied sciences;Casting;Composites;Deformation;Dispersion strengthening;Elasticity. Plasticity;Exact sciences and technology;Holography;Mechanical properties and methods of testing. Rheology. Fracture mechanics. Tribology;Mechanical properties at ambient temperature;Metallic glasses;Metals. Metallurgy;Strain rate;Thermoplastic forming;Yield strength;Zirconium base alloys
Date:	2012-09-25
Issue Date:	2026-04-23 11:49:15 (UTC+8)
Publisher:	Elsevier BV;Kidlington: Elsevier B.V
Abstract:	摘要： Compressive flow stress clearly decreases with lower compressive strain rate as well as higher compression temperature, as shown in (a) The lowest flow stress, 76MPa, can be obtained at 764K with strain rate of 5×10−2s−1. A submicron-scaled hologram pattern was replicated by hot pressing the Zr-based BMGC plate against a die engraved with submicron-scaled groove at 756K as illustrated in (b). The enlarged SEM image of the replicated hologram pattern in (c) shows grooves about 0.6μm in depth, indicating relatively good microforming ability for this Zr47.3Cu32Al8Ag8Ta4Si0.7-based BMGC in the SCL region. [Display omitted] ► Deformation behavior of the Zr-based BMGC within the SCL region reveals that a relatively low viscosity between 108 and 1010Pas. ► More than 60% plastic strain can be obtained readily by compression test at the temperatures within SCL region under different strain rates. ► All evidences of the XRD analysis and TEM characterization confirms that the amorphous phase in Zr4-based BMGC would keep stable after hot compression. ► A strain rate sensitivity exponent (m) more than 0.35 was measures for the Zr-based BMGC deformed at 756K, and 764K. ► The imprinted hologram pattern with 0.6μm depth grooves demonstrates relatively good microforming ability for this Zr-based BMGC. The thermoplastic deformation behavior of a Zr47.3Cu32Al8Ag8Ta4Si0.7-based bulk metallic glass composite (BMGC) is studied using thermal mechanical analyzer (TMA) and high temperature compression test in the supercooled liquid (SCL) region. The deformation behavior of the Zr47.3Cu32Al8Ag8Ta4Si0.7-based BMGC rod is investigated using TMA under compression at different strain rates (5×10−2 to 5×10−1s−1) and at different temperatures above the onset temperature of viscous-flow (∼740 to 764K) in the SCL region. It is observed that, at a constant strain rate of 5×10−2s−1, the flow stress decreases with increasing temperature and reaches a relatively low value about 76MPa at 764K. In parallel, the value of flow stress increases with increasing strain rate at the same testing temperature. A satisfactory thermoplastic forming ability of the Zr47.3Cu32Al8Ag8Ta4Si0.7-based BMGC in the SCL region is demonstrated by imprinting the hologram pattern. 出版者： Kidlington: Elsevier B.V 出版日期： 2012-09-25 出處： Journal of alloys and compounds, 2012-09, Vol.536, p.S165-S170 版權： 2012 Elsevier B.V. 版權： 2015 INIST-CNRS 識別號： ISSN: 0925-8388 識別號： EISSN: 1873-4669 識別號： DOI: 10.1016/j.jallcom.2012.01.020
Appears in Collections:	[Institute of Materials Science and Engineering] journal & Dissertation