Growth and properties of single-crystalline Ge nanowires and germanide/Ge nano-heterostructures

NCUIR > College of Electrical Engineering & Computer Science > Department of Electrical Engineering > journal & Dissertation > Item 987654321/107342

Please use this identifier to cite or link to this item: https://ir.lib.ncu.edu.tw/handle/987654321/107342

Title:	Growth and properties of single-crystalline Ge nanowires and germanide/Ge nano-heterostructures
Authors:	辛正倫;Tsai, Cheng-Yu;Yu, Shih-Ying;Hsin, Cheng-Lun;Huang, Chun-Wei;Wang, Chun-Wen;Wu, Wen-Wei
Contributors:	資訊電機學院電機工程學系
Date:	2012-01-07
Issue Date:	2026-04-23 14:09:40 (UTC+8)
Publisher:	Royal Society of Chemistry
Abstract:	摘要： Single-crystalline Ge nanowires have been synthesized on Au-coated Si substrates through a thermal evaporation, condensation method and vapor-liquid-solid mechanism. The [111] growth direction of the Ge nanowires was analyzed using HRTEM and fast Fourier transform diffraction patterns. Global back-gated Ge nanowire field-effect transistors (FETs) on the Si 3 N 4 dielectrics were fabricated and studied, showing p-type behavior and a field effect hole mobility of 44.3 cm 2 V −1 s −1 . The Ge channel length could be well controlled through the annealing process. After a rapid thermal annealing (RTA) process, Ni 2 Ge/Ge/Ni 2 Ge nano-heterostructures were formed. The electrical transport properties were effectively improved by the heterojunction rather than the metal contact. The epitaxial relationship between Ge and orthorhombic Ni 2 Ge was Ge[110]//Ni 2 Ge[110] and Ge(-11-1)//Ni 2 Ge(1-1-2). From electrical transport properties, the measured resistivity of the Ge nanowires was much lower than intrinsic bulk Ge material. A room temperature photoluminescence spectrum of the Ge nanowires possessed a broad blue emission with a peak at 462 nm in wavelength, which was attributed to the oxide-related defect states. Due to the existence of the defects, a Ge nanowire FET was able to detect visible light and serve as a nanowire photodetector. The growth and electrical transport properties of single-crystalline Ge nanowires and germanide/Ge nano-heterostructures are discussed. Due to the existence of defects, a Ge nanowire field-effect transistor was able to serve as a photodetector. 出版日期： 2011-12-05 資源來源： Royal Society of Chemistry 識別號： EISSN: 1466-8033 識別號： DOI: 10.1039/c1ce06107k