Electrochemical behavior of anodized AA6063-T6 alloys affected by matrix structures

NCU Institutional Repository > 工學院 > 機械工程學系 > 期刊論文 > Item 987654321/108788

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://ir.lib.ncu.edu.tw/handle/987654321/108788

题名:	Electrochemical behavior of anodized AA6063-T6 alloys affected by matrix structures
作者:	施登士;Huang, Yung-Sen;Shih, Teng-Shih;Wu, Chen-En
贡献者:	工學院機械工程學系
关键词:	Al(OH)3;AlOOH;Anodic aluminum oxide film;Cold rolled;Condensed matter: electronic structure, electrical, magnetic, and optical properties;Condensed matter: structure, mechanical and thermal properties;Cross-disciplinary physics: materials science;rheology;EIS;Exact sciences and technology;Physics;XPS
日期:	2013-01-01
上传时间:	2026-04-23 15:06:16 (UTC+8)
出版者:	Elsevier;Amsterdam: Elsevier B.V
摘要:	摘要： ► Deformation after solution treatment introduced Al matrix to have deformation bands and few Si particles. ► Dislocations remained in the matrix lift up field potential and produce AlOOH oxide in the AAO film. ► The silicon-containing particles were found to trap in the AAO film. ► The silicon particles and the Al(OOH) oxide is significantly to influence the electrochemical behavior of AAO films. AA 6063 alloys were cold-rolled (CR) either before or after solution treatment (S) and then different samples were artificially aged (T6) to obtain different samples (CRST6 and SCRT6). The highest dislocation density was observed in the SCRT6 sample which also showed the lowest particle count among the three samples; ST6, CRST6 and SCRT6. Subsequently, all samples were anodized in a 15wt% sulfuric acid solution for different time spans to obtain anodic aluminum oxide (AAO) films. The anodized samples were further analyzed with X-ray Photoelectron Spectroscopy (XPS) analysis. We determined that the constituent phases in the AAO film were composed of hydrated amorphous alumina, hydrated oxide (Al(OH)3) and oxyhydroxide (AlOOH) phases together with some silicon-containing particles trapped in the films on all samples. In the electrochemical test, the silicon-containing particles and hydrated Al(OH)3 oxide that existed at the electrolyte/film (e/f) interface were found to inversely influence the corrosion resistance of the anodized samples. 出版者： Amsterdam: Elsevier B.V 出版日期： 2013-01-01 出處： Applied Surface Science, 2013-01, Vol.264, p.410-418 版權： 2012 Elsevier B.V. 版權： 2014 INIST-CNRS 識別號： ISSN: 0169-4332 識別號： EISSN: 1873-5584 識別號： DOI: 10.1016/j.apsusc.2012.10.036
显示于类别:	[機械工程學系] 期刊論文