Electrochemical behavior of anodized AA7075-T73 alloys as affected by the matrix structure

NCUIR > Engineering College > Departmant of Mechanical Engineering > journal & Dissertation > Item 987654321/108791

Please use this identifier to cite or link to this item: https://ir.lib.ncu.edu.tw/handle/987654321/108791

Title:	Electrochemical behavior of anodized AA7075-T73 alloys as affected by the matrix structure
Authors:	施登士;Huang, Yung-Sen;Shih, Teng-Shih;Chou, Jun-Hung
Contributors:	工學院機械工程學系
Keywords:	AAO films;Alloys;Aluminum base alloys;Anodizing;Cold rolling;Condensed matter: electronic structure, electrical, magnetic, and optical properties;Condensed matter: structure, mechanical and thermal properties;Cross-disciplinary physics: materials science;rheology;Exact sciences and technology;Intermetallic compound;Liquid nitrogen;Microhardness;Microstructure;Physics;Potentiodynamic polarization test;Precipitates;Precipitation
Date:	2013-10-15
Issue Date:	2026-04-23 15:06:37 (UTC+8)
Publisher:	Elsevier;Amsterdam: Elsevier B.V
Abstract:	摘要： •Cryo-rolling before solution treatment can significantly reduce the intermetallic compound particle size.•The silicon-containing lumps and air-pockets were found to be trapped in the AAO film after anodization for 15min.•The anodized samples that cryo-rolled before solution treatment performed excellent in corrosion resistance. A set of standard 7075-T73 alloy samples was prepared for comparison with samples that had been cold-rolled before the T73 treatment. One set of samples was subjected to cold rolling at room temperature and another deep-cooled in liquid nitrogen prior to rolling. Both sets of samples were then subjected to a T73 treatment. The microstructure of the different samples was observed and their micro-hardness was tested and recorded. The samples that had first been subjected to the deep-cooling treatment prior to rolling and T73 treatment (CRST73) showed few subgrains and smaller amounts of second phase particles in the matrix than was the case with the other two sets of samples. The experimental results also indicated that the matrix of the CRST73 samples mostly displayed disk-like precipitates of Mg2Zn and Al2Cu. After anodization, this batch of samples demonstrated superior corrosion resistance and the lowest passive current density during potentiodynamic polarization testing. 出版者： Amsterdam: Elsevier B.V 出版日期： 2013-10-15 出處： Applied Surface Science, 2013-10, Vol.283, p.249-257 版權： 2013 Elsevier B.V. 版權： 2014 INIST-CNRS 識別號： ISSN: 0169-4332 識別號： DOI: 10.1016/j.apsusc.2013.06.094