Taylor and Francis Ltd.;United States: Taylor & Francis Group
摘要:
摘要： In this study, an iron oxide magnetic microparticles and poly(dimethylsiloxane) (MMPs-PDMS) composite material was employed to demonstrate a simple high-strength reversible magnetic bonding method. This paper presents the casting of opaque-view (where optical inspection through the microchannels was impossible) and clear-view (where optical inspection through the microchannel was possible) MMPs-PDMS. The influence of the microchannel geometries on the casting of the opaque-view casting was limited, which is similar to standard PDMS casting. Clear-view casting performance was highly associated with the microchannel geometries. The effects of the microchannel layout and the gap between the PDMS cover layer and the micromold substrate were thoroughly investigated. Compared with the native PDMS bonding strength of 31 kPa, the MMPs-PDMS magnetic bonding experiments showed that the thin PDMS film with an MMPs-PDMS layer effectively reduced the surface roughness and enhanced MMPs-PDMS reversible magnetic bonding strength. A thin PDMS film-coated opaque-view MMPs-PDMS device exhibited the greatest bonding strength of 110 kPa, and a clear-view MMPs-PDMS device with a thin PDMS film attained a magnetic bonding strength of 81 kPa. 其他題名： Sci Technol Adv Mater 出版者： United States: Taylor & Francis Group 出版日期： 2016-01-01 出處： Science and technology of advanced materials, 2016-01, Vol.17 (1), p.2-11 資源來源： Taylor & Francis Journals Auto-Holdings Collection 版權： 2016 The Author(s). Published by National Institute for Materials Science in partnership with Taylor & Francis 2016 版權： 2016 The Author(s). Published by National Institute for Materials Science in partnership with Taylor & Francis. This work is licensed under the Creative Commons Attribution License http://creativecommons.org/licenses/by/4.0/ (the “License”). Notwithstanding the ProQuest Terms and Conditions, you may use this content in accordance with the terms of the License. 版權： 2016 The Author(s). Published by National Institute for Materials Science in partnership with Taylor & Francis 2016 The Author(s) 識別號： ISSN: 1468-6996 識別號： ISSN: 1878-5514 識別號： EISSN: 1878-5514 識別號： DOI: 10.1080/14686996.2016.1140301 識別號： PMID: 27877852