Effects of poly(vinyl alcohol) content and calcination temperature on the characteristics of unsupported alumina membrane

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26599

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26599

題名:	Effects of poly(vinyl alcohol) content and calcination temperature on the characteristics of unsupported alumina membrane
作者:	Yang,WP;Shyu,SS;Lee,ES;Chao,AC
貢獻者:	化學工程與材料工程學系
關鍵詞:	INORGANIC MEMBRANES;CERAMIC MEMBRANES;POROUS ALUMINA;SOL;GELS;SEPARATION;ALKOXIDES
日期:	1996
上傳時間:	2010-06-29 17:32:02 (UTC+8)
出版者:	中央大學
摘要:	Nonsupported alumina porous membranes without pinholes or cracks were prepared by the sol-gel process using aluminum sec-butoxide as the starting material. The effects of using different PVA contents at various calcination temperatures on the characteristics of the membrane were investigated by scanning electron microscopy and nitrogen sorption porosimetry. The results after calcining at 450 degrees C for 5 hours showed that the range of pore size distributions increases with increasing PVA concentration. The active nucleus numbers of phase transition to alpha-alumina decreased as the content of PVA increased at about 1050 degrees C. The morphology of unsupported alumina membranes was affected by the PVA concentration and calcination temperature.