    題名: SURFACE MODIFICATION OF KEVLAR 149 FIBERS BY GAS PLASMA TREATMENT .1. MORPHOLOGY AND SURFACE CHARACTERIZATION
    作者: SHEU,GS;SHYU,SS
    貢獻者: 化學工程與材料工程學系
    關鍵詞: ARAMID FIBERS;MATRIX INTERFACE;EPOXY COMPOSITES;POLYETHYLENE;POLYSTYRENE;SIMS
    日期: 1994
    上傳時間: 2010-06-29 17:34:20 (UTC+8)
    出版者: 中央大學
    摘要: Kevlar 149 fibers have been surface treated with NH3-, O2-, or H2O-plasma to modify the fiber surfaces. SEM (scanning electron microscopy) is used to characterize the surface topography of fibers etched by gas plasmas. The chemical compositions and functional groups of the fiber surfaces are identified by ESCA (electron spectroscopy for chemical analysis) and SSIMS (static secondary ion mass spectroscopy), respectively. The contact angle of water on modified PPTA [poly(p-phenylene terephthalamide)] film prepared from using Kevlar 149 fibers is also used to investigate the wettability. The results show that the etching abilities of gas plasmas are dependent on the type of gas used for plasma treatments. The contact angle data indicate that all the three gas plasma treatments are effective in rendering the surface of PPTA more hydrophilic. The ESCA analysis results show that the surface compositions of plasma-treated fibers are highly dependent on the type of gas used and treatment time. Changes in surface compositions of fibers treated by NH3-, O2-, and H2O-plasma are observed. Increasing nitrogen and oxygen contents are observed for the NH3-Plasma treatment, and the O2- and H2O-plasma treatments, respectively. Furthermore, the incorporation of amino groups into fiber surfaces by NH3-plasma treatment and the extensive damage of the aromatic ring and the polymer backbone by H2O-plasma and O2-plasma are evidenced by SSIMS.
    關聯: JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
    顯示於類別:[化學工程與材料工程研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML391檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋  - 隱私權政策聲明