    題名: SURFACE MODIFICATION OF KEVLAR-149 FIBERS BY GAS PLASMA TREATMENT .2. IMPROVED INTERFACIAL ADHESION TO EPOXY-RESIN
    作者: SHEU,GS;SHYU,SS
    貢獻者: 化學工程與材料工程學系
    關鍵詞: ACID-BASE INTERACTIONS;ARAMID FIBERS;MATRIX INTERFACE;ORGANIC FIBERS;SHEAR-STRENGTH;CONTACT ANGLES;CARBON-FIBERS;COMPOSITES;WETTABILITY;PROPERTY
    日期: 1994
    上傳時間: 2010-06-29 17:34:22 (UTC+8)
    出版者: 中央大學
    摘要: Kevlar 149 fibers were surface-modified by NH3, O2, and H2O plasmas to improve the adhesion to epoxy resin. Poly(p-phenylene terephthalamide) (PPTA) film prepared from Kevlar 149 fibers was also modified to estimate the changes in surface energy caused by the plasma treatments. The interfacial shear strength (IFSS) between the fiber and epoxy resin was measured by the microbond pull-out test. The fracture surfaces of microbond pull-out specimens were examined by scanning electron microscopy (SEM) to identify the failure mode of the microcomposites. The results showed that the IFSS of the Kevlar 149 fiber/epoxy resin system was remarkably improved (up to a factor of 2.42) by these plasma treatments and the treatment time was the governing factor in improving the IFSS. After the plasma treatments, the fracture mode of the microcomposites changed from failure at the interface to failure either in the fiber skin or in the epoxy resin. The surface free energy and the work of adhesion of water on the PPTA surface were markedly improved by the plasma treatments. The polar component of the surface free energy and the acid-base (non-dispersion) component of the work of adhesion made an important contribution to the improvement. Some correlations between the IFSS and the surface energies were found.
    關聯: JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY
    顯示於類別:[化學工程與材料工程研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML358檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋  - 隱私權政策聲明