PLASMA SURFACE TREATMENTS OF CARBON-FIBERS .2. INTERFACIAL ADHESION WITH POLY(PHENYLENE SULFIDE)

NCU Institutional Repository > 工學院 > 化學工程與材料工程研究所 > 期刊論文 > Item 987654321/26733

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26733

題名:	PLASMA SURFACE TREATMENTS OF CARBON-FIBERS .2. INTERFACIAL ADHESION WITH POLY(PHENYLENE SULFIDE)
作者:	YUAN,LY;SHYU,SS;LAI,JY
貢獻者:	化學工程與材料工程學系
關鍵詞:	SHEAR-STRENGTH;MICROBOND METHOD;GRAPHITE FIBERS;RESIN INTERFACE;EPOXY;POLYMERIZATION
日期:	1992
上傳時間:	2010-06-29 17:35:27 (UTC+8)
出版者:	中央大學
摘要:	Type I and type II carbon fibers were covered with a thin plasma polymer film and etched by an oxygen or an argon plasma to reinforce the interfacial adhesion with poly(phenylene sulfide). Plasma etching of the fibers increased the interfacial shear strength up to 2.5 times which is much better than plasma polyacrylonitrile deposited fibers. Electron spectroscopy for chemical analysis surface analyses show different mechanisms of adhesion enhancement. Film deposited fibers which possess more abundant oxygen functionalities and aromatics show improved adhesion. On the other hand, increased adhesion with etched fibers occurs as a result of a larger area of unoxidized carbon structure. Surface nitrogen atoms also play a role in the interfacial adhesion.