Permeability of coating in the lost foam casting process

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/26933

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26933

题名:	Permeability of coating in the lost foam casting process
作者:	Chang,AS;Shih,TS
贡献者:	機械工程研究所
关键词:	N/A
日期:	1999
上传时间:	2010-06-29 18:03:36 (UTC+8)
出版者:	中央大學
摘要:	This study measured the pressures developed during a filling experiment using molten grey iron in the lost foam casting (LFC) process. The measured pressures included back pressure and permeable pressure. The back pressure is created in-mould from the metal-foam interface. The permeable pressure was measured on the mould side of the coating, when gases introduced from the decomposing EPS were permeating through the coating. The permeable pressure reflected the permeability of the coating while filling molten iron. Variables, which included particle sizes, types of binders, weight per cent of binder in coatings, influenced the permeability of coating at room temperature and at casting temperature. Coatings made from flaky alumina developed a greater total length of pore channels than those made from angular silica, Increasing the particle size of the refractory increased the permeability of the coating at room temperature. The highest permeable pressure was measured when the particle size was 74 mu m and acrylic resin was used as a binder. The optimum binder content was less than 1% for flaky alumina and acrylic resin binder, The optimum coating thickness was less than 0.5 mm to develop a maximum permeable pressure associated with a minimum back pressure in the mould.
關聯:	INTERNATIONAL JOURNAL OF CAST METALS RESEARCH
显示于类别:	[機械工程研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	541	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing

数据加载中.....