Wear and corrosion behaviors of SiCp reinforced copper matrix composite formed by hot pressing

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/26949

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26949

題名:	Wear and corrosion behaviors of SiCp reinforced copper matrix composite formed by hot pressing
作者:	Lee,YF;Lee,SL;Lin,JC
貢獻者:	機械工程研究所
關鍵詞:	SLIDING WEAR;ALUMINUM
日期:	1999
上傳時間:	2010-06-29 18:03:57 (UTC+8)
出版者:	中央大學
摘要:	Wear and corrosion behaviors of SiCp reinforced copper matrix composite formed by hot pressing were studied. The results show that the tensile strength, hardness and material porosity increased with the increase of SiCp content. The wear rate of Cu/SiCp composites decreased with the increase of SiCp content, applied load and high sliding velocity (exceeds 300 rpm). In contrast the wear rate of Cu/SiCp composites increased with low sliding velocity (100 rpm to 300 rpm). A dramatic wear rate of Cu/SiCp, composite is observed at the initial wear stage (0-400m). However, when sliding distance exceeds 800 m, the wear behavior becomes more stable. In addition, the corrosion resistance of Cu/SiC, composite in 5% NaCl solution increases with increasing pH value, but decreases with increasing SiCp content. Pits always initiate at the interfacial boundary between SiCp and copper, which makes SiCp particles peeling and copper matrix pitting deeply.
關聯:	SCANDINAVIAN JOURNAL OF METALLURGY
顯示於類別:	[機械工程研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	464	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing