Effects of Be addition on microstructures and mechanical properties of B319.0 alloys

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/26960

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/26960

题名:	Effects of Be addition on microstructures and mechanical properties of B319.0 alloys
作者:	Wamg,PS;Liauh,YJ;Lee,SL;Lin,JC
贡献者:	機械工程研究所
关键词:	AL-SI ALLOYS;HEAT-TREATMENT;A357 ALLOYS;FE;DISSOLUTION;PHASE;IRON
日期:	1998
上传时间:	2010-06-29 18:04:14 (UTC+8)
出版者:	中央大學
摘要:	An investigation of iron intermetallics, silicon particles and strengthening precipitates on the microstructures and mechanical properties in B319.0 alloys has been performed. Distinct morphologies were discerned between Be-containing and Be-free alloys at various solution temperatures. Solution treatment was carried out in the temperature range 480 degrees C-530 degrees C for 8 h. Dissolution of the iron intermetallics takes place at temperatures close to 510 degrees C. through fragmentation of the phases. The dissolution of iron intermetallics is accelerated with increasing solution temperature. The addition of Be to the alloy will raise the Al-Al-2 Cu eutectic melting temperature to 522 degrees C compared with 515 degrees C for Be-free alloys. The Be-free alloys show larger amounts of iron intermetallics than the Be-containing alloys. The addition of Be can change the platelet-like shape of iron intermetallic phases to a comparatively harmless Chinese-script shape. Also, the amount of iron-bearing phases and silicon particles are lower and silicon particles are smaller and more spherical in the Be-containing alloys. Small amounts of Be in B319.0 alloys can also increase the precipitation kinetics of strengthening precipitates. Tensile properties could be improved with optimal solution treatment and the addition of Be. (C) 1998 Elsevier Science S.A. All rights reserved.
關聯:	MATERIALS CHEMISTRY AND PHYSICS