Effects of beryllium on fatigue crack propagation of A357 alloys containing iron

NCU Institutional Repository > 工學院 > 機械工程研究所 > 期刊論文 > Item 987654321/27033

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/27033

題名:	Effects of beryllium on fatigue crack propagation of A357 alloys containing iron
作者:	Tan,YH;Lee,SL;Wu,HY
貢獻者:	機械工程學系
關鍵詞:	MG-SI ALLOY;FRACTURE-BEHAVIOR;MICROSTRUCTURE;GROWTH
日期:	1996
上傳時間:	2010-06-29 18:06:03 (UTC+8)
出版者:	中央大學
摘要:	An investigation of iron-bearing compounds, silicon particles and Mg2Si precipitates on fatigue crack growth behaviour in A357 alloys has been performed. The effect of Be on increasing Delta K-th is more apparent in alloys with higher Fe content than in alloys with medium and lower Fe content. The fatigue life of the higher and medium Fe-content Be-containing alloys will be improved much as well as that of in the lower Fe content of alloys. Major fatigue cracks induced by cracking of iron-bearing compounds cracking were found in the medium and higher Fe-content alloys. In the lower Fe-content alloys, irregular silicon particles appear to be the main source of fatigue crack nucleation. In region I of low fatigue crack growth rates, the higher threshold stress intensity is attributed to the greater mechanical strength and to enhanced roughness-induced crack closure and deflection from more tortuous crack paths. The superior fatigue crack propagation resistance at higher growth rates of regions II and III is attributed to greater fracture toughness and to reduced crack growth rates in the Be-containing alloys regardless of Fe levels. The fracture surface morphologies of near-threshold crack growth contain stepped patterns and cleavage-like facets. With increasing crack growth rate, the fracture surface roughness increases and striations are formed in region II. At higher fatigue crack growth rates, the formation of a dimple surface and cleavage plane replaces striation formation.
關聯:	INTERNATIONAL JOURNAL OF FATIGUE
顯示於類別:	[機械工程研究所] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	489	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing

資料載入中.....