Thermal reliability and characterization of InGaP Schottky contact with Ti/Pt/Au metals

NCU Institutional Repository > 理學院 > 光電科學研究所 > 期刊論文 > Item 987654321/28204

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/28204

题名:	Thermal reliability and characterization of InGaP Schottky contact with Ti/Pt/Au metals
作者:	Lee,CT;Shiao,HP;Yeh,NT;Tsai,CD;Lyu,YT;Tu,YK
贡献者:	光電科學研究所
关键词:	EPITAXY
日期:	1997
上传时间:	2010-06-29 19:43:49 (UTC+8)
出版者:	中央大學
摘要:	We present the characteristics of Ti/Pt/Au Schottky contacts on wide bandgap InGaP semiconductors with surface pre-treatment before Schottky contact deposition, and investigate the influence of post heat treatment on Schottky diodes. With the pre-deposition surface etching by dilute HCl, dilute NH4OH, or buffer oxide etchant (BOE), the performance of Schottky diodes compared with samples without surface pre-treatment is improved significantly. Auger electron spectroscopy (AES) analysis of the thermally annealed Schottky diode has been performed to investigate the failure mechanism. No significant change was found for samples annealed up to 450 degrees C. However, a drastic degradation of the barrier height and the ideality factor was observed in samples annealed at 500 degrees C, which may be caused by the interdiffusion and penetration of metals into the semiconductor. Copyright (C) 1996 Elsevier Science Ltd
關聯:	SOLID-STATE ELECTRONICS
显示于类别:	[光電科學研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	561	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing