Morphology and optical properties of zinc oxide thin films grown on Si (100) by metal-organic chemical vapor deposition

NCU Institutional Repository > 理學院 > 物理研究所 > 期刊論文 > Item 987654321/38959

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/38959

題名:	Morphology and optical properties of zinc oxide thin films grown on Si (100) by metal-organic chemical vapor deposition
作者:	Lan,SM;Uen,WY;Chan,CE;Chang,KJ;Hung,SC;Li,ZY;Yang,TN;Chiang,CC;Huang,PJ;Yang,MD;Chi,GC;Chang,CY
貢獻者:	物理研究所
關鍵詞:	QUANTUM DOTS;ZNO;PHOTOLUMINESCENCE;TEMPERATURE;NANOWIRES;SAPPHIRE
日期:	2009
上傳時間:	2010-07-08 14:00:25 (UTC+8)
出版者:	中央大學
摘要:	Undoped zinc oxide (ZnO) thin films were deposited on Si (100) substrates by atmospheric pressure metal-organic chemical vapor deposition (AP-MOCVD). After a nucleation layer of ZnO about 500 A... was deposited, top ZnO films with 320-440 nm in thickness were fabricated at temperatures varying from 450 to 600 A degrees C, respectively. X-ray diffraction analyses demonstrate that all the films grown have polycrystalline wurtzite structure. Scanning electron microscopy observations indicate that ZnO films grow with c-axis aligned grains when the deposition temperature is lower than 600 A degrees C. However, 3D microstructures without c-axis alignment were found when the film was deposited at 600 A degrees C. Room temperature photoluminescence (PL) spectra peaking at 3.27-3.29 eV were observed for the ZnO films grown at 450-600 A degrees C. However, only the spectrum from the film grown at 600 A degrees C could present a high intensity ratio of the ultraviolet band to deep-level emissions, which is above 392 and show a minimum full-width at half-maximum of 99 meV for the ultraviolet band. Temperature-dependent PL measurements from 20 to 300 K exhibited the luminescent mechanism of the present ZnO films to be near band excitonic emission.
關聯:	JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
顯示於類別:	[物理研究所] 期刊論文