DEPOSITION OF HYDROGENATED AMORPHOUS-CARBON AND SILICON CARBON THIN-FILMS IN LOW-ENERGY RF MAGNETRON PLASMAS

NCU Institutional Repository > 理學院 > 物理研究所 > 期刊論文 > Item 987654321/39349

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/39349

题名:	DEPOSITION OF HYDROGENATED AMORPHOUS-CARBON AND SILICON CARBON THIN-FILMS IN LOW-ENERGY RF MAGNETRON PLASMAS
作者:	I,L;WU,MS
贡献者:	物理研究所
关键词:	ION-BEAM DEPOSITION;ARGON GAS-MIXTURES;DIAMONDLIKE CARBON;ALLOY;HARD;ABSORPTION;RESONANCE
日期:	1992
上传时间:	2010-07-08 14:13:00 (UTC+8)
出版者:	中央大學
摘要:	Studies have been made of the room temperature deposition of hydrogenated amorphous carbon and hydrogenated amorphous silicon-carbon in a magnetron discharge system at low ion energy (E(i) approximately 30 eV), high density (n(e) approximately 10(11) cm-3) and low pressure (approximately 5 m Torr) with CH4/Ar and CH4/SiH4/Ar gas mixtures respectively. A gas flow rate modulation technique was introduced to investigate the effect of low energy Ar ion bombardment immediately after the deposition of ultra-thin films. The plasma created a highly reactive environment and the deposition process had high gas conversion efficiency and good uniformity. Both carbon and silicon-carbon films were smooth with good adhesion. Absorption from the C-CH3 mode and some from the C=CH2 mode were found in the IR spectra of the carbon film. The IR spectra of the silicon-carbon film were mainly contributed by the SiHx, Si-CH3 and CHn related modes, and showed higher carbon incorporation than those obtained from the conventional discharge system. The strengths of the SiC and CHn modes and their ratio could be increased by increasing the methane to silane partial pressure ratio or the effective RF power. The index of refraction decreased with the increasing carbon incorporation. The film with alternating deposition of ultra-thin (20-75 angstrom) a-SixC1-x film and Ar plasma bombardment cycles showed that the post-deposition, low energy ion bombardment does not change the film thickness but is sufficient to crack the hydrocarbon bonds and promote the formation of Si-CHn bonds on the top few tens of monolayers of the ultra-thin film.