    題名: Effects of Cu content on microstructure and mechanical properties of Al-14.5Si-0.5Mg alloy
    作者: Wu,CT;Lee,SL;Hsieh,MH;Lin,JC
    貢獻者: 機械工程學系
    關鍵詞: CASTING ALLOYS;HEAT-TREATMENT;A357 ALLOYS;BERYLLIUM;ADDITIONS;BEHAVIOR;MG;PHASE;TRACE;IRON
    日期: 2010
    上傳時間: 2012-03-27 17:02:44 (UTC+8)
    出版者: 國立中央大學
    摘要: This study elucidates how Cu content affects the microstructure and mechanical properties of Al-14 5Si-0 5Mg alloy by adding 465 wt % and 0 52 wt % Cu Different Fe bearing phases were found in the two alloys The acicular beta Al(5)FeSi was found only in the high Cu alloy In the low Cu alloy Al(8)Mg(3)FeSi(6) was the Fe bearing phase Tensile testing indicated that the low Cu alloy containing Al(8)Mg(3)FeSi(6) had higher UTS and elongation than the high Cu alloy containing the acicular beta Al(5)FeSi It is believed that the presence of the acicular p Al5FeSi in the high Cu alloy increased the number of crack initiators and brittleness of the alloy Increasing Cu content in the Al-14 5Si-0 5Mg alloy also promoted solution hardening and precipitation hardening under as quenched and aging conditions respectively The hardness of the high Cu alloy therefore exceeded that of low Cu alloy (C) 2010 Elsevier Inc All rights reserved
    關聯: MATERIALS CHARACTERIZATION
    顯示於類別:[機械工程學系] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML431檢視/開啟


    在NCUIR中所有的資料項目都受到原著作權保護.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 隱私權政策聲明