    题名: Nanoindentation-Induced Structural Deformation in GaN/AIN Multilayers
    作者: Jian,SR;Juang,JY;Chen,NC;Jang,JSC;Huang,JC;Lai,YS
    贡献者: 機械工程學系
    关键词: TRANSMISSION ELECTRON-MICROSCOPY;GAN THIN-FILMS;CHEMICAL-VAPOR-DEPOSITION;BERKOVICH NANOINDENTATION;SPHERICAL INDENTATION;MECHANICAL DEFORMATION;INTERMEDIATE LAYER;SI;MICROSTRUCTURES;BEHAVIORS
    日期: 2010
    上传时间: 2012-03-27 17:03:56 (UTC+8)
    出版者: 國立中央大學
    摘要: The mechanical responses of GaN/AIN multilayers grown on Si(111) substrates by using the metal-organic vapor phase epitaxy (MOVPE) were investigated by combining the Berkovich nanoindentation and the cross-sectional transmission electron microscopy (XTEM) techniques. The prominent mechanical parameters such as the hardness and Young's modulus of GaN/AIN multilayers were obtained to be 21.6 +/- 0.8 GPa and 285.7 +/- 12.1 GPa, respectively by operating the Berkovich nanoindenter with the continuous contact stiffness measurements (CSM) mode. The structural deformation behaviors were delineated by XTEM observations taken in the vicinity regions just underneath the indenter tip. It was revealed that the "pop-ins" observed in the load displacement curve during loading are due primarily to the activities of dislocation nucleation and propagation. There is no evidence of either phase transformation or micro-crack formation observed in XTEM images of GaN/AIN multilayers, which is consistent with no distinct "pop-out" event displayed in unloading curves.
    關聯: NANOSCIENCE AND NANOTECHNOLOGY LETTERS
    显示于类别:[機械工程學系] 期刊論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML267检视/开启


    在NCUIR中所有的数据项都受到原著作权保护.

    社群 sharing

    ::: Copyright National Central University. | 國立中央大學圖書館版權所有 | 收藏本站 | 設為首頁 | 最佳瀏覽畫面: 1024*768 | 建站日期:8-24-2009 :::
    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈  - 隱私權政策聲明