Anisotropic and tensile flow behaviors of Mg alloy AZ31B thin sheet in H24 condition at elevated temperatures

NCU Institutional Repository > 工學院 > 機械工程學系 > 期刊論文 > Item 987654321/50197

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/50197

题名:	Anisotropic and tensile flow behaviors of Mg alloy AZ31B thin sheet in H24 condition at elevated temperatures
作者:	Wu,HY;Sun,PH;Lin,FZ
贡献者:	機械工程學系
关键词:	WROUGHT MAGNESIUM ALLOY;AL-ZN ALLOY;DYNAMIC RECRYSTALLIZATION;DEFORMATION MECHANISMS;PLASTIC-DEFORMATION;TEXTURE EVOLUTION;ROOM-TEMPERATURE;NONBASAL SLIP;SUPERPLASTICITY;DIFFRACTION
日期:	2011
上传时间:	2012-03-27 17:06:12 (UTC+8)
出版者:	國立中央大學
摘要:	In this work, a series of experiments was performed to explore the effects of anisotropy, strain rate, and temperature on microstructure change and associated mechanical response of a rolled AZ31B-H24 Mg alloy sheet under tension. Tensile tests were carried out on specimens in the 0, 45, and 900 to the rolling direction, using initial strain rates in the range of 4 x 10(-3) to 1 x 10(-1) s(-1) at temperatures of 250 and 370 degrees C. Results showed that variations in flow behavior under tension could be related to the changes in microstructure resulting from applied tensile conditions. Resultant microstructures, such as degree of dynamic recrystallization, grain growth, and shape of the grain, were associated with temperature, strain rate, and tensile loading direction. The initial texture influenced the variations in changes in microstructure and mechanical properties upon testing in different directions. The specimens upon testing in the 45 degrees to the rolling direction yielded higher m-value, lower strength, and greater elongation to failure under all test conditions. (C) 2010 Elsevier B.V. All rights reserved.
關聯:	MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
显示于类别:	[機械工程學系] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	477	检视/开启

在NCUIR中所有的数据项都受到原著作权保护.

社群 sharing

数据加载中.....