HF/H(2)O(2) Etching for Removal of Damage Layer on As-Transferred Si Layer Formed by Ion-Cut Process

NCU Institutional Repository > 理學院 > 物理學系 > 期刊論文 > Item 987654321/52762

請使用永久網址來引用或連結此文件: http://ir.lib.ncu.edu.tw/handle/987654321/52762

題名:	HF/H(2)O(2) Etching for Removal of Damage Layer on As-Transferred Si Layer Formed by Ion-Cut Process
作者:	Ho,CC;Huang,CH;Chen,BS;Su,YH;Chen,KJ;Hsu,CS;Lee,TH
貢獻者:	物理學系
日期:	2010
上傳時間:	2012-06-11 10:43:06 (UTC+8)
出版者:	國立中央大學
摘要:	When a 100 nm thick Si layer was transferred onto a bare Si wafer by the hydrogen-induced-layer-transfer process, a spongy damage layer with microvoids was formed on the transferred layer because of hydrogen blistering. The surface-to-volume ratio of the damage layer was greater than that of the layer where blistering did not occur. Therefore, the damage layer was selectively etched by an HF/H(2)O(2) mixture and completely removed (the etching rates of Si at 70 degrees C for the bulk layer and damage layer were 0.45 and 13.8 nm/min, respectively). Consequently, a smooth, damage-free Si layer (root-mean-square roughness = 2.74 nm) was obtained. (C) 2010 The Electrochemical Society. [DOI: 10.1149/1.3397476] All rights reserved.
關聯:	ELECTROCHEMICAL AND SOLID STATE LETTERS
顯示於類別:	[物理學系] 期刊論文

文件中的檔案:

檔案	描述	大小	格式	瀏覽次數
index.html		0Kb	HTML	469	檢視/開啟

在NCUIR中所有的資料項目都受到原著作權保護.

社群 sharing